Multifaceted coating system
View Patent ↗A protective coating system that exhibits a plurality of highly desirable characteristics, such as broad range adhesion, fire retardancy, anti-microbial, anti-graffiti, and solvent resistance, is provided. The coating composition generally includes a urethane resin, mono and multifunctional monomers, a reactive diluent, and fire-retardant and antimicrobial agents. The coating compositions are particularly suited for use with wallpaper and other paper and plastic products, especially those having images printed thereon.
1. A protective coating composition comprising:
from 3 wt. % to 30 wt. % of one or more urethane resins;
from 10 wt. % to 35 wt. % of one or more monofunctional acrylate monomers;
from 5 wt. % to 25 wt. % of one or more multifunctional monomers;
from 5 wt. % to 25 wt. % of a vinyl-based reactive diluent monomer;
from 10 wt. % to 50 wt. % of a fire-retardant additive; and
from 0.01 wt. % to 5 wt. % of an antimicrobial agent,
said composition having a viscosity of about 200 to about 400 cps, measured at 25° C. using a Brookfield viscometer.
2. The composition according to claim 1 , wherein said one or more urethane resins are selected from the group consisting of polyester-based aliphatic urethane resins, aliphatic urethane resins, aromatic urethane resins, acrylic-based urethane resins, urethane acrylate resins, and epoxy-based urethane resins.
3. The composition according to claim 1 , wherein said one or more multifunctional monomers comprises a difunctional acrylate monomer.
4. The composition according to claim 1 , wherein said fire-retardant additive comprises a phosphate-based flame retardant.
5. The composition according to claim 1 , wherein said fire-retardant additive is non-halogenated.
6. The composition according to claim 1 , wherein said antimicrobial agent comprises silver or silver ions.
7. The composition according to claim 1 , wherein said composition is UN-curable and comprises a photoinitiator.
8. The composition according to claim 1 , wherein said composition when applied to and cured upon a surface of a textile or film at a coating thickness of at least 0.5 mil protects said surface such that when exposed to an open flame according to NFPA 701 produces an after flame duration of less than 2.0 seconds and/or a char length of less than 6.5 in.
9. The composition according to claim 1 , wherein said composition when applied to and cured upon a surface of a substrate at a coating thickness of at least 0.5 mil is capable of at least 3-log reduction of K. pneumoniae Methicillin Resistant S. aureus (MRSA), Clostridium difficile, S. epidermidis, A. baumannii, C. albicans, E. coli, P. aeruginosa, S. aureus, Enterococcus spp. (e.g., Vancomycin Resistant Enterococcus faecalis (VRE)), Candida spp., and CoNS according to Japanese Industrial Standard (JIS) Z 2801.
10. The composition according to claim 1 , wherein said composition when applied to and cured upon a surface of a substrate at a coating thickness of at least 0.5 mil is capable of withstanding at least 50 rubs with acetone-soaked cotton.
11. An article having at least a portion of the outer surface thereof coated with the protective coating composition according to claim 1 .
12. The article according to claim 11 , wherein said article is wallpaper.
13. The article according to claim 11 , wherein said article outer surface comprises an ink image imprinted thereon.
14. The article according to claim 11 , wherein said article comprises a synthetic resin material or a coated board stock material.
15. A method of forming a protective coating on an article comprising the steps of:
applying to at least a portion of the surface of said article the coating composition according to claim 1 ; and
curing said coating composition on said surface to form a protective layer thereon.
16. The method according to claim 15 , wherein said method comprises printing an image onto said surface prior to applying said coating composition thereto.
17. The method according to claim 15 , wherein said step of applying said coating to said surface comprises screen printing; roller coating, or curtain coating said coating composition onto said surface.
18. The method according to claim 15 , wherein said step of curing said coating composition comprises exposing said coating composition to a source of UV light.
19. The composition according to claim 1 , wherein said composition is a clear composition.