Adhesive composition, adhesive layer, optical member, and adhesive sheet
An adhesive composition, an adhesive layer, an optical member, and an adhesive sheet, the adhesive composition including 100 parts by weight of a (meth)acrylic copolymer, the (meth)acrylic copolymer having a weight average molecular weight of about 100,000 to about 2,000,000 g/mol; about 0.05 to about 5 parts by weight of a carbodiimide crosslinker; and about 0.01 to about 0.3 parts by weight of an organic group-containing compound, the organic group-containing compound including at least one selected from the group of titanium, zirconium, and hafnium.
1. An adhesive layer having a 7-day gel fraction that is within about ±5% of a 0.5-day gel fraction and the 0.5-day gel fraction of about 50% to about 95%, the 7-day gel fraction being measured after storage under conditions of about 23° C. and about 50% RH for about 7 days, and the 0.5-day gel fraction being measured after storage under conditions of about 23° C. and about 50% RH for about 0.5 days,
wherein the adhesive layer is prepared from an adhesive composition including:
100 parts by weight of a (meth)acrylic copolymer,
about 0.05 to about 5 parts by weight of a carbodiimide crosslinker, and
about 0.01 to about 0.3 parts by weight of an organic group-containing compound, the organic group-containing compound including at least one selected from the group of titanium and zirconium.
2. The adhesive layer as claimed in claim 1 , wherein the (meth)acrylic copolymer is prepared from a monomer mixture including:
about 0.1 to about 9 parts by weight of a carboxyl group-containing monomer,
0 to about 1 part by weight of a hydroxyl group-containing (meth)acrylic monomer, and
about 90 to about 99.9 parts by weight of a (meth)acrylic acid ester monomer, a total amount of the carboxyl group-containing monomer, the hydroxyl group-containing (meth)acrylic monomer, and the (meth)acrylic acid ester monomer being 100 parts by weight.
3. The adhesive layer as claimed in claim 1 , further comprising about 0.05 to about 5 parts by weight of an isocyanate crosslinker.
4. The adhesive layer as claimed in claim 1 , further comprising a silane coupling agent.
5. The adhesive layer as claimed in claim 1 , further comprising an imidazole compound represented by Formula 1:
wherein R 1 , R 2 , and R 3 are each independently a hydrogen atom, a halogen atom, or a substituted or unsubstituted C1 to C10 linear or branched alkyl group.
6. The adhesive layer as claimed in claim 5 , wherein the imidazole compound is present in the composition an amount of about 0.008 to about 0.2 parts by weight.
7. The adhesive layer as claimed in claim 1 , wherein the adhesive composition has a viscosity (v1) 12 hours after preparation that is less than about 10% greater than a viscosity (v0) immediately after preparation.
8. An optical member comprising the adhesive layer as claimed in claim 1 .
9. The optical member as claimed in claim 8 , wherein:
the (meth)acrylic copolymer has a weight average molecular weight of about 2,000,000 to about 1,800,000 g/mol, and
the adhesive layer has an adhesive strength of about 0.5 to about 9 N/25 mm according to JIS Z0237.
10. The optical member as claimed in claim 8 , wherein the adhesive layer has an adhesive strength of about 0.5 to about 9 N/25 mm according to JIS Z0237.
11. An adhesive sheet comprising the adhesive layer as claimed in claim 1 .
12. The adhesive sheet as claimed in claim 11 , wherein:
the (meth)acrylic copolymer has a weight average molecular weight of about 100,000 to about 1,000,000 g/mol, and
the adhesive layer has an adhesive strength of about 0.05 to about 20 N/25 mm according to JIS Z0237.
13. The adhesive sheet as claimed in claim 11 , wherein the adhesive layer has an adhesive strength of about 0.05 to about 20 N/25 mm according to JIS Z0237.