Rapid manufacturing of porous metal prostheses
An orthopaedic prosthesis and a method for rapidly manufacturing the same are provided. The orthopaedic prosthesis includes a solid bearing layer, a porous bone-ingrowth layer, and an interdigitating layer therebetween. A laser sintering technique is performed to manufacture the orthopaedic prosthesis.
1. A method of rapidly manufacturing an orthopaedic prosthesis having a porous substrate, the porous substrate including an outer surface and a plurality of ligaments that define pores beneath the outer surface, the method comprising the steps of:
depositing a plurality of metal powder particles onto the outer surface of the porous substrate;
allowing at least a first portion of the plurality of metal powder particles to enter the pores beneath the outer surface of the porous substrate, the first portion of the plurality of metal powder particles being sized to fit within the pores of the porous substrate; and
applying an energy source to the first portion of the plurality of metal powder particles to form solid metal, the solid metal interdigitating into the pores of the porous substrate.
2. The method of claim 1 , wherein the energy source comprises a laser.
3. The method of claim 1 , wherein a second portion of the plurality of metal powder particles is located at or beyond the outer surface of the porous substrate.
4. The method of claim 3 , wherein, after the applying step, the second portion of the plurality of metal powder particles is converted to solid metal to form a solid bearing layer on the porous substrate.
5. The method of claim 1 , wherein the plurality of metal powder particles comprise titanium or a titanium alloy.
6. The method of claim 1 , wherein the plurality of ligaments of the porous substrate comprise tantalum.
7. The method of claim 1 , wherein the pores of the porous substrate are about 500 micrometers in size.
8. The method of claim 1 , wherein the plurality of metal powder particles are each less than about 30 micrometers in size.
9. The method of claim 1 , wherein the porous substrate has a porosity of 55% to 90%.
10. The method of claim 9 , wherein the plurality of ligaments of the porous substrate comprise tantalum.
11. The method of claim 1 , wherein the porous substrate has a porosity of 65% to 85%.
12. A method of rapidly manufacturing an orthopaedic prosthesis having a solid metal component and a porous metal component, the porous metal component including a plurality of ligaments that define pores, the method comprising the steps of:
depositing a plurality of metal powder particles into the pores of the porous metal component; and
directing an energy source into the pores of the porous metal component to convert the plurality of metal powder particles in the pores to solid metal in the pores, the solid metal in the pores coupling the solid metal component to the porous metal component.
13. The method of claim 12 , wherein the plurality of metal powder particles has a lower melting point than the plurality of ligaments of the porous metal component.
14. The method of claim 13 , wherein the directing step melts the plurality of metal powder particles located in each pore without melting the plurality of ligaments that surround the pore.
15. The method of claim 12 , wherein the solid metal in the pores and the solid metal component have the same elemental content.
16. The method of claim 12 , wherein the porous metal component has a porosity of 55% to 90%.
17. The method of claim 16 , wherein the plurality of ligaments of the porous metal component comprise tantalum.
18. The method of claim 12 , wherein the porous metal component has a porosity of 65% to 85%.