Ni-based alloy, and turbine rotor and stator blade for gas turbine
View Patent ↗A Ni-based alloy including chromium, cobalt, aluminum, titanium, tantalum, tungsten, molybdenum, niobium, carbon, and boron, the balance being nickel and incidental impurities, is provided. The alloy has an alloy composition of, on the basis of mass percent, chromium: 13.10% to 16.00%, cobalt: 8.00% to 12.50%, aluminum: 2.30% to 3.50%, titanium: 4.80% to 5.50%, tantalum: 0.40% to less than 1.00%, tungsten: 4.50% to 6.00%, molybdenum: 0.10% to 1.50%, niobium: 0.60% to 1.70%, carbon: 0.01% to 0.20%, boron: 0.005% to 0.02%, and the balance: nickel and incidental impurities.
1. A Ni-based alloy comprising chromium, cobalt, aluminum, titanium, tantalum, tungsten, molybdenum, niobium, carbon, and boron, the balance being nickel and incidental impurities,
wherein the alloy has an alloy composition of, on the basis of mass percent, chromium: 13.10% to 16.00%, cobalt: 8.00% to 12.50%, aluminum: 2.30% to 3.50%, titanium: 4.80% to 5.50%, tantalum: 0.40% to less than 1.00%, tungsten: 4.50% to 6.00%, molybdenum: 0.10% to 1.50%, niobium: 0.60% to 1.70%, carbon: 0.01% to 0.20%, boron: 0.005% to 0.02%, and the balance: nickel and incidental impurities.
2. The Ni-based alloy according to claim 1 , further comprising one kind or more elements selected from the group of hafnium, rhenium, zirconium, oxygen and nitrogen,
wherein the alloy has the alloy composition of, on the basis of mass percent, hafnium: 0% to 2.00%, rhenium: 0% to 0.50%, zirconium: 0% to 0.05%, oxygen: 0% to 0.005%, and nitrogen: 0% to 0.005%.
3. The Ni-based alloy according to claim 2 ,
wherein the alloy has the alloy composition of, on the basis of mass percent, hafnium: 0% to 0.10%, rhenium: 0% to 0.10%, zirconium: 0% to 0.03%, oxygen: 0% to 0.005%, and nitrogen: 0% to 0.005%.
4. The Ni-based alloy according to claim 1 ,
wherein in a diagram showing a relationship of an amount of tantalum+niobium and an amount of tungsten, the composition is in a composition range enclosed by a line sequentially connecting a point A (1.5%, 4.5%), a point B (2.5%, 4.5%), a point C (2.5%, 5.5%) and a point D (1.5%, 6.0%) which are represented by (tantalum+niobium amount, tungsten amount).
5. The Ni-based alloy according to claim 1 ,
wherein the alloy has the alloy composition of, on the basis of mass percent, chromium: 13.10% to 14.30%, cobalt: 8.50% to 11.00%, aluminum: 2.70% to 3.40%, titanium: 4.80% to 5.30%, tantalum: 0.50% to 0.90%, tungsten: 4.80% to 5.50%, molybdenum: 0.60% to 1.40%, niobium: 0.70% to 1.60%, carbon: 0.10% to 0.18%, and boron: 0.01% to 0.02%.
6. The Ni-based alloy according to claim 5 ,
wherein the alloy has the alloy composition of, on the basis of mass percent, chromium: 13.70% to 14.10%, cobalt: 9.10% to 10.80%, aluminum: 3.00% to 3.40%, titanium: 4.80% to 5.10%, tantalum: 0.60% to 0.90%, tungsten: 4.80% to 5.40%, molybdenum: 0.70% to 1.30%, niobium: 0.80% to 1.50%, carbon: 0.12% to 0.17%, and boron: 0.01% to 0.02%.
7. A cast product, comprising the Ni-based alloy according to claim 1 .
8. A turbine rotor blade for a gas turbine, comprising the Ni-based alloy according to claim 1 .
9. A gas turbine using the gas turbine rotor blade or stator blade according to claim 8 .
10. A turbine stator blade for a gas turbine, comprising the Ni-based alloy according to claim 1 .
11. A gas turbine using the gas turbine rotor blade or stator blade according to claim 10 .