Process for the manufacture of lenses
View Patent ↗Process for manufacturing of an optical article which comprises: making available an organic substrate based on an organic polymer having a degree of water uptake of greater than or equal to 0.6% by weight, with respect to the total weight of the substrate, the degree of water uptake being equal to the weight of water absorbed by the material after drying and then storing for 800 hours in a chamber at 50° C. under a relative humidity of 100% and at atmospheric pressure; forming a hard abrasion-resistant coating on the substrate by heating the substrate at a temperature of greater than or equal to 90° C. for a period of time of at least 20 minutes; exposing the substrate covered with the hard abrasion-resistant coating to a humid atmosphere, so as to restore, to the organic substrate, the water evaporated during stage; and depositing of a water-impermeable inorganic coating by vacuum evaporation.
1. The process for the manufacture of an optical article, which comprises:
making available an organic substrate based on an organic polymer having a degree of water uptake of greater than or equal to 0.6% by weight, with respect to the total weight of said substrate, chosen from the group formed by acrylic and methacrylic homopolymers and copoloymers, thioacrylic and thiomethacrylic homopolymers and copolymers, polyvinylbutyral (PVB), polyurethanes, polythiourethanes, homopolymers and copolymers based on polyol allyl carbonates, thermoplastic ethylene/vinyl acetate (EVA) copolymers, polyesters, polyepoxides, polyamides, polycarbonate/polyester copolymers, cycloolefin copolymers and the combinations of these polymers, the degree of water uptake being equal to the weight of water absorbed by the material after drying and then storing for 800 hours in a chamber of 50° C. under a relative humidity of 100% and at atmospheric pressure;
a stage of formulation of a hard abrasion-resistant coating on said organic substrate, this stage comprising the heating of the substrate at a temperature of greater than or equal to 90° C. for a period of time of at least 20 minutes;
a stage of exposure of the organic substrate covered with the hard abrasion-resistant coating to a humid atmosphere at a duration of between 1 and 20 days, so as to restore, to the organic substrate, the water evaporated during the formation stage; and
a stage of deposition of a water-impermeable inorganic coating by vacuum evaporation.
2. The process according to claim 1 , wherein the organic polymer is chosen from thermoset polythiourethanes.
3. The process according to claim 2 , wherein the relative humidity of the humid atmosphere of the exposure stage is between 50 and 80%.
4. The process according to claim 1 , wherein the relative humidity of the humid atmosphere of the exposure stage is between 50 and 80%.
5. The process according to claim 1 , wherein the exposure stage is carried out at a temperature of between 15 and 80° C.