Rubber composition including a phenolic resin
View Patent ↗A rubber composition which can be used in particular in tires, based on at least one diene elastomer, one reinforcing filler, one crosslinking system, one phenolic resin and one polyaldehyde. The use of a polyaldehyde makes it possible to advantageously replace conventional methylene donors while preventing the production of formaldehyde during the vulcanization of the rubber compositions and thus to limit the environmental impact of these compounds. Furthermore, these polyaldehyde compounds make it possible not only to obtain rubber compositions exhibiting the same low-strain stiffness as conventional rubber compositions using HMT or H3M methylene donors but also, surprisingly, to greatly improve the fatigue strength of the rubber compositions and thus the endurance of the tires.
1. A rubber composition comprising:
a diene elastomer;
a reinforcing filler;
a crosslinking system;
a phenolic resin;
a polyaldehyde wherein the amount of the phenolic resin is between 1 and 20 phr and wherein the amount of polyaldehyde is between 1 and 20 phr,
wherein the functional groups of the polyaldehyde compound react with the carbon atoms of the phenolic resin, thereby creating a reinforcing resin network.
2. The rubber composition according to claim 1 , wherein the elastomer is chosen from the group consisting of natural rubber, synthetic polyisoprenes, polybutadienes, butadiene copolymers, isoprene copolymers and the mixtures of these elastomers.
3. The rubber composition according to claim 1 , wherein the amount of phenolic resin is between 2 and 15 phr.
4. The rubber composition according to claim 1 , wherein the polyaldehyde comprises at least two aldehyde functional groups.
5. The rubber composition according to claim 1 , wherein the amount of polyaldehyde is between 1 and 15 phr.
6. The rubber composition according to claim 1 , wherein the polyaldehyde is 2-hydroxybenzene-1,3,5-tricarbaldehyde.
7. The rubber composition according to claim 1 , wherein the reinforcing filler comprises carbon black and/or silica.
8. A tire comprising the rubber composition according to claim 1 .
9. A finished or semifinished rubber article comprising the rubber composition according to claim 1 .
10. A process for preparing the rubber composition according to claim 1 , comprising the steps of:
incorporating a reinforcing filler, a phenolic resin and a polyaldehyde in a diene elastomer during a first stage (“nonproductive” stage), everything being kneaded thermomechanically until a maximum temperature of between 110° C. and 190° C. is reached;
cooling the combined mixture to a temperature of less than 100° C.;
subsequently incorporating, during a second stage (“productive” stage), a crosslinking system; and
kneading everything up to a maximum temperature of less than 110° C.
11. A process for preparing the rubber composition according to claim 1 , comprising the steps of:
incorporating a reinforcing filler in a diene elastomer during a first stage (“nonproductive” stage), everything being kneaded thermomechanically until a maximum temperature of between 110° C. and 190° C. is reached;
cooling the combined mixture to a temperature of less than 100° C.;
subsequently incorporating, during a second stage (“productive” stage), a crosslinking system, a phenolic resin and a polyaldehyde; and
kneading everything up to a maximum temperature of less than 110° C.
12. A process for preparing the rubber composition according to claim 1 , comprising the steps of:
incorporating a reinforcing filler and a phenolic resin in a diene elastomer during a first stage (“nonproductive” stage), everything being kneaded thermomechanically until a maximum temperature of between 110° C. and 190° C. is reached;
cooling the combined mixture to a temperature of less than 100° C.;
subsequently incorporating, during a second stage (“productive” stage), a crosslinking system and a polyaldehyde; and
kneading everything up to a maximum temperature of less than 110° C.