Positive electrode active substance particles and process for producing the same, and non-aqueous electrolyte secondary battery
Positive electrode active substance particles including a compound having at least a crystal system belonging to a space group of R−3m and a crystal system belonging to a space group of C2/m, and boron. The compound is a composite oxide comprising at least Li, Mn, and Co and/or Ni; a relative intensity ratio [(a)/(b)] of a maximum diffraction peak intensity (a) observed at 2θ=20.8±1° in a powder X-ray diffraction pattern of the positive electrode active substance as measured using a Cu-Ku ray to a maximum diffraction peak intensity (b) observed at 2θ=18.6±1° in the powder X-ray diffraction pattern, is 0.02 to 0.5; a content of Mn in the positive electrode active substance particles such that a molar ratio of Mn/(Ni+Co+Mn) is not less than 0.55; and the positive electrode active substance particles include boron in an amount of 0.001 to 3% by weight.
1. Positive electrode active substance particles comprising a compound having at least a crystal system belonging to a space group of R−3m and a crystal system belonging to a space group of C2/m, and boron,
which compound is a composite oxide comprising at least Li, Mn, and Co and/or Ni;
which positive electrode active substance particles whose relative intensity ratio [(a)/(b)] of a maximum diffraction peak intensity (a) observed at 2θ=20.8±1° in a powder X-ray diffraction pattern of the positive electrode active substance as measured using a Cu-Ka ray to a maximum diffraction peak intensity (b) observed at 2θ=18.6±1° in the powder X-ray diffraction pattern, is 0.02 to 0.5;
a content of Mn in the positive electrode active substance particles being controlled such that a molar ratio of Mn/(Ni+Co+Mn) therein is not less than 0.56; and
which positive electrode active substance particles comprise the boron in an amount of 0.001 to 3% by weight,
wherein the positive electrode active substance particles have a molar ratio of Li/(Ni+Co+Mn) of 1.23 to 1.7.
2. Positive electrode active substance particles according to claim 1 , wherein the positive electrode active substance particles comprise LiMxMn 1-x O 2 wherein M is Ni and/or Co; 0<x≦1, as a compound having a crystal system belonging to a space group of R−3m, and Li 2 M′ (1-y) Mn y O 3 wherein M′ is Ni and/or Co; 0<y≦1, as a compound having a crystal system belonging to a space group of C2/m.
3. Positive electrode active substance particles according to claim 1 , wherein the positive electrode active substance particles have a specific surface area of 0.05 to 20 m 2 /g as measured by a BET method.
4. Positive electrode active substance particles according to claim 1 , wherein the positive electrode active substance particles are in the form of secondary particles produced by aggregating primary particles thereof in which the primary particles have an average primary particle diameter of not more than 3 μm, and the secondary particles have an average secondary particle diameter of 1 to 50 μm.
5. A process for producing the positive electrode active substance particles as defined in claim 1 , comprising the step of calcining a mixture comprising precursor particles comprising Mn, and Ni and/or Co, a lithium compound and a boron compound at a temperature of 500 to 1500° C., wherein a content of Mn in the precursor particles comprising Mn, and Ni and/or Co is controlled such that a molar ratio of Mn/(Ni+Co+Mn) therein is not less than 0.56.
6. A non-aqueous electrolyte secondary battery comprising a positive electrode comprising the positive electrode active substance particles as defined in claim 1 .