Polypropylene resin expanded particles and polypropylene resin in-mold foaming molded body
Polypropylene resin expanded particles include polypropylene resin as base material resin having at least two melting peaks on a DSC curve, the at least two melting peaks including (i) a lowest-temperature melting peak of 100° C. or more but 130° C. or less and (ii) a highest-temperature melting peak of 140° C. or more but 160° C. or less, so that the expanded particles: produce an in-mold foaming molded product at a very low mold heating steam pressure; exhibit low distortion, low shrinkage, and a wide range of heating condition for molding, even if the mold heating steam pressure is increased; have satisfactory moldability when the expanded particles are molded by using a mold having a complicated shape or a large mold; and maintain properties such as compressive strength, substantially unimpaired, when the expanded particles make the in-mold foaming molded product.
1. Polypropylene resin expanded particles, comprising:
a polypropylene resin as a base material resin which has at least three melting peaks on a DSC curve obtained by measurements of melting points with use of a differential scanning calorimeter, the DSC curve being obtained in a second temperature rise in raising a temperature of the polypropylene resin from 20° C. to 220° C. at a heating rate of 10° C./min, lowering the temperature from 220° C. to 20° C. at a cooling rate of 10° C./min, and raising the temperature again from 20° C. to 220° C. at a heating rate of 10° C./min, the at least three melting peaks including (i) a lowest-temperature melting peak of 100° C. or more but 130° C. or less and (ii) a highest-temperature melting peak of 140° C. or more but 160° C. or less.
2. The polypropylene resin expanded particles as set forth in claim 1 ,
wherein the at least three melting peaks include (i) the lowest-temperature melting peak, (ii) the highest-temperature melting peak, and (iii) a melting peak between the lowest-temperature melting peak and the highest-temperature melting peak.
3. The polypropylene resin expanded particles as set forth in claim 1 , wherein the lowest-temperature melting peak derived from a polypropylene resin polymerized by using a metallocene polymerization catalyst.
4. The polypropylene resin expanded particles as set forth in claim 3 ,
wherein the lowest-temperature melting peak and the highest-temperature melting peak are derived from the polypropylene resin polymerized by using the metallocene polymerization catalyst.
5. The polypropylene resin expanded particles as set forth in claim 3 ,
wherein the metallocene polymerization catalyst contains a metallocene compound represented by the following Formula 1:
where R 1 , R 2 , R 3 , R 4 , R 5 , R 6 , R 7 , R 8 , R 9 , R 10 , R 11 , R 12 , R 13 , and R 14 identically or independently one selected from the group consisting of a hydrogen atom, a hydrocarbon group, and a silicon-containing group; M represents a group-4 transition metal; Y represents a carbon atom or a silicon atom; Q is identically or independently one selected from the group consisting of a halogen atom, a hydrocarbon group, an anion ligand, and a neutral ligand coordinatable with a lone pair of electrons; and j is an integer of 1 to 4.
6. The polypropylene resin expanded particles as set forth in claim 1 ,
wherein the polypropylene resin expanded particles have at least two melting peaks on the DSC curve obtained in first measurement of temperature rise of the polypropylene resin expanded particles with use of a differential scanning calorimeter, the at least two melting peaks including (i) a lowest-temperature melting peak of 100° C. or more but 130° C. or less and (ii) a highest-temperature melting peak of 140° C. or more but 160° C. or less.
7. The polypropylene resin expanded particles as set forth in claim 6 ,
wherein a difference between the temperature of the lowest-temperature melting peak and the temperature of the highest-temperature melting peak is 25° C. or more but 40° C. or less.
8. A polypropylene resin in-mold foaming molded product prepared from the polypropylene resin expanded particles as set forth in claim 1 by in-mold foaming molding.
9. A method for producing polypropylene resin expanded particles, comprising the steps of:
dispersing polypropylene resin particles together with a dispersant in water in a presence of a foaming agent in a vessel, the polypropylene resin particles containing a polypropylene resin as a base material resin, the polypropylene resin having at least three melting peaks on a DSC curve obtained by measurements of melting points with use of a differential scanning calorimeter, the at least three melting peaks including (i) a lowest-temperature melting peak of 100° C. or more but 130° C. or less and (ii) a highest-temperature melting peak of 140° C. or more but 160° C. or less;
heating the polypropylene resin particles to a foaming temperature under pressure, and impregnating the foaming agent to the polypropylene resin particles; and thereafter
releasing and foaming a dispersion substance including the polypropylene resin particles in the vessel to a low pressure area while keeping a temperature and pressure in the vessel constant, so that the polypropylene resin expanded particles are obtained, wherein
the polypropylene resin expanded particles, comprising:
a polypropylene resin as a base material resin which has at least three melting peaks on a DSC curve obtained by measurements of melting points with use of a differential scanning calorimeter, the DSC curve being obtained in a second temperature rise in raising a temperature of the polypropylene resin from 20° C. to 220° C. at a heating rate of 10° C./min, lowering the temperature from 220° C. to 20° C. at a cooling rate of 10° C./min, and raising the temperature again from 20° C. to 220° C. at a heating rate of 10° C./min, the at least three melting peaks including (i) a lowest-temperature melting peak of 100° C. or more but 130° C. or less and (ii) a highest- temperature melting peak of 140° C. or more but 160° C. or less.
10. A method for producing a polypropylene resin in-mold foaming molded product, comprising the step of in-mold foaming molding the polypropylene resin expanded particles produced by the method as set forth in claim 9 .
11. A method for producing polypropylene resin expanded particles, comprising the steps of:
dispersing polypropylene resin particles together with a dispersant in water in a presence of a foaming agent in a vessel, the polypropylene resin particles containing a polypropylene resin as a base material resin, the polypropylene resin being obtained by means of multi-stage polymerization and having at least three melting peaks on a DSC curve obtained by measurements of melting points with use of a differential scanning calorimeter, the at least two melting peaks including (i) a lowest-temperature melting peak of 100° C. or more but 130° C. or less and (ii) a highest-temperature melting peak of 140° C. or more but 160° C. or less;
heating the polypropylene resin particles to a foaming temperature under pressure, and impregnating the foaming agent to the polypropylene resin particles; and thereafter
releasing and foaming a dispersion substance including the polypropylene resin particles in the vessel to a low pressure area while keeping a temperature and pressure in the vessel constantly, so that the polypropylene resin expanded particles are obtained, wherein
the polypropylene resin expanded particles, comprising:
a polypropylene resin as a base material resin which has at least three melting peaks on a DSC curve obtained by measurements of melting points with use of a differential scanning calorimeter, the DSC curve being obtained in a second temperature rise in raising a temperature of the polypropylene resin from 20° C. to 220° C. at a heating rate of 10° C./min, lowering the temperature from 220° C. to 20° C. at a cooling rate of 10° C./min, and raising the temperature again from 20° C. to 220° C. at a heating rate of 10° C./min, the at least three melting peaks including (i) a lowest-temperature melting peak of 100° C. or more but 130° C. or less and (ii) a highest-temperature melting peak of 140° C. or more but 160° C. or less.
12. The method as set forth in claim 11 , wherein the multi-stage polymerization is performed by using a metallocene catalyst.