Rubber composition comprising a 1,2,4-triazine
View Patent ↗A rubber composition for the manufacture of tires, based on one or more diene elastomers, on one or more reinforcing fillers and on a vulcanization system, characterized in that the said vulcanization system comprises one or more 1,2,4-triazine compounds of formula:
1. A rubber composition for the manufacture of tires, based on one or more diene elastomers, on one or more reinforcing fillers and on a vulcanization system, wherein the vulcanization system comprises one or more 1,2,4-triazine compounds of formula:
where
R 1 and R 2 independently represent H or a —C 1 -C 25 — hydro carbon group chosen from linear, branched or cyclic alkyl groups and aryl groups, optionally interrupted by one or more heteroatoms, it being possible for R 1 and R 2 to together form a ring,
R 3 represents:
a linear or branched —C 1 -C 25 — alkyl group which is optionally interrupted by one or more heteroatoms and which is optionally substituted by one or more cyclic —C 3 -C 10 — alkyl or —C 6 -C 12 — aryl groups, or
a cyclic —C 3 -C 10 — alkyl group which is optionally interrupted by one or more heteroatoms and which is optionally substituted by one or more linear, branched or cyclic —C 1 -C 25 — alkyl or —C 6 -C 12 — aryl groups which are optionally interrupted by one or more heteroatoms.
2. The composition according to claim 1 , wherein R 1 and R 2 independently represent H, a methyl group or a phenyl group.
3. The composition according to claim 2 , wherein R 1 or R 2 represents a phenyl group.
4. The composition according to claim 3 , wherein R 1 represents a hydrogen and R 2 represents a phenyl group.
5. The composition according to claim 1 , wherein R 3 represents a cyclohexyl group or a tert-butyl group.
6. The composition according to claim 1 , wherein the 1,2,4-triazine compound or compounds represent from 0.1 to 10 phr.
7. The composition according to claim 1 , wherein the diene elastomer or elastomers are chosen from the group consisting of polybutadienes, natural rubber, synthetic polyisoprenes, butadiene copolymers, isoprene copolymers and the mixtures of these elastomers.
8. The composition according to claim 7 , wherein the diene elastomer is a blend of natural rubber with a polybutadiene and a butadiene/styrene copolymer, or a blend of a polybutadiene and a butadiene/styrene copolymer.
9. The composition according to claim 1 , wherein the reinforcing filler or fillers are chosen from silica, carbon black and their mixtures.
10. The composition according to claim 1 , wherein the reinforcing filler or fillers are present at a level of between 20 and 200 phr.
11. A process for preparing a rubber composition for the manufacture of tires as defined in claim 1 , comprising the steps of:
incorporating the reinforcing filler or fillers in the diene elastomer or elastomers, during a “non-productive” stage, everything being kneaded thermomechanically, in one or more goes, until a maximum temperature of between 130° C. and 200° C. is reached,
cooling the combined mixture to a temperature of less than 100° C.,
subsequently incorporating, a “productive” stage, the vulcanization system and then kneading everything up to a maximum temperature of less than 120° C.
12. Finished article or semi-finished product intended for a motor vehicle ground-contact system, comprising a composition according to claim 1 .
13. Tire, comprising a rubber composition as defined in claim 1 .
14. The composition according to claim 1 , wherein the 1,2,4-triazine compound or compounds represent from 0.5 to 7 phr.
15. The composition according to claim 1 , wherein the 1,2,4-triazine compound or compounds represent from 0.5 to 5 phr.
16. The composition according to claim 1 , wherein the reinforcing filler or fillers are present at a level of between 30 and 150 phr.