Polypropylene resin, polypropylene resin composition, and foam-injection-molded article
View Patent ↗A polypropylene resin and a polypropylene resin composition are provided, which have excellent fluidity and foaming properties, and particularly in use for foam injection molding, allow molding with a narrow initial cavity clearance even if a large mold is used, and therefore can provide a thin, large-area foam-injection-molded article having good appearance. The invention relates to a polypropylene resin obtained by melt mixing a linear polypropylene resin, a radical polymerization initiator and a conjugated diene compound, wherein the polypropylene resin has a melt flow rate of more than 30 g/10 min and not more than 250 g/10 min as measured at 230° C. under a load of 2.16 kg; a melt tension at 200° C. of not less than 0.3 cN; and a loss tangent (tan δ) of not more than 6.0, the loss tangent being a ratio of loss modulus to storage modulus at an angular frequency of 1 rad/s in dynamic viscoelasticity measurement at 200° C., and also relates to a polypropylene resin composition for foam injection molding, containing the polypropylene resin.
1. A polypropylene resin, obtained by melt mixing a linear polypropylene resin, a radical polymerization initiator and a conjugated diene compound,
wherein said polypropylene resin has a melt flow rate of more than 50 g/10 min and not more than 250 g/10 min as measured at 230° C. under a load of 2.16 kg; a melt tension at 200° C. of not less than 0.3 cN; and a loss tangent, tan δ, of not more than 6.0, the loss tangent being a ratio of loss modulus to storage modulus at an angular frequency of 1 rad/s in dynamic viscoelasticity measurement at 200° C.
2. The polypropylene resin according to claim 1 ,
wherein the amount of the radical polymerization initiator added is not less than the amount of the conjugated diene compound added.
3. The polypropylene resin according to claim 2 ,
wherein the amount of the radical polymerization initiator added is not less than 1.5 times the amount of the conjugated diene compound added.
4. A polypropylene resin composition for foam injection molding, comprising:
3 to 50% by weight of a polypropylene resin; and
50 to 97% by weight of a first linear polypropylene resin having a melt flow rate at 230° C. of not less than 10 g/10 min and not more than 150 g/10 min and a melt tension of less than 2 cN,
wherein said polypropylene resin is obtained by melt mixing a second linear polypropylene resin, a radical polymerization initiator and a conjugated diene compound, and
wherein said polypropylene resin has a melt flow rate of more than 30 g/10 min and not more than 250 g/10 min as measured at 230° C. under a load of 2.16 kg; a melt tension at 200° C. of not less than 0.3 cN; and a loss tangent, tan δ, of not more than 6.0, the loss tangent being a ratio of loss modulus to storage modulus at an angular frequency of 1 rad/s in dynamic viscoelasticity measurement at 200° C.
5. The polypropylene resin composition for foam injection molding according to claim 4 ,
wherein the first linear polypropylene resin has a Charpy impact strength at 23° C. of not less than 5 kJ/m 2 .
6. An foam-injection-molded article, comprising:
a composition comprising a polypropylene resin or a polypropylene resin composition for foam injection molding, and
a foaming agent,
wherein said polypropylene resin composition for foam injection molding comprises
3 to 50% by weight of the polypropylene resin; and
50 to 97% by weight of a first linear polypropylene resin having a melt flow rate at 230° C. of not less than 10 g/10 min and not more than 150 g/10 min and a melt tension of less than 2 cN,
wherein said polypropylene resin is obtained by melt mixing a second linear polypropylene resin, a radical polymerization initiator and a conjugated diene compound, and
wherein said polypropylene resin has a melt flow rate of more than 30 g/10 min and not more than 250 g/10 min as measured at 230° C. under a load of 2.16 kg; a melt tension at 200° C. of not less than 0.3 cN; and a loss tangent, tan δ, of not more than 6.0, the loss tangent being a ratio of loss modulus to storage modulus at an angular frequency of 1 rad/s in dynamic viscoelasticity measurement at 200° C., and
wherein said foam-injection molded article is produced by foam injection molding said composition.
7. The polypropylene resin according to claim 4 ,
wherein the melt flow rate is more than 50 g/10 min and not more than 250 g/10 min.
8. The polypropylene resin according to claim 4 ,
wherein the amount of the radical polymerization initiator added is not less than the amount of the conjugated diene compound added.
9. The polypropylene resin according to claim 8 ,
wherein the amount of the radical polymerization initiator added is not less than 1.5 times the amount of the conjugated diene compound added.
10. The polypropylene resin according to claim 5 ,
wherein the melt flow rate is more than 50 g/10 min and not more than 250 g/10 min.
11. The polypropylene resin according to claim 5 ,
wherein the amount of the radical polymerization initiator added is not less than the amount of the conjugated diene compound added.
12. The polypropylene resin according to claim 11 ,
wherein the amount of the radical polymerization initiator added is not less than 1.5 times the amount of the conjugated diene compound added.
13. The polypropylene resin according to claim 6 ,
wherein the melt flow rate is more than 50 g/10 min and not more than 250 g/10 min.
14. The polypropylene resin according to claim 6 ,
wherein the amount of the radical polymerization initiator added is not less than the amount of the conjugated diene compound added.
15. The polypropylene resin according to claim 14 ,
wherein the amount of the radical polymerization initiator added is not less than 1.5 times the amount of the conjugated diene compound added.