Heterophasic polypropylene resin
View Patent ↗Heterophasic polypropylene resin comprising a propylene random copolymer matrix phase (A), and an ethylene-propylene copolymer rubber phase (B) dispersed within the matrix phase wherein the heterophasic polypropylene resin has a MFR (2.16 kg, 230° C.) of 1.0 to 100 g/10 min, determined according to ISO 1133, and a fraction soluble in p-xylene at 25° C. (XCS fraction) which is present in the resin in an amount of 28 to 50 wt %, and which has a molecular weight distribution (M w /M n ) of 1.0 to 4.0.
1. Heterophasic polypropylene resin comprising
a propylene random copolymer matrix phase (A), and
an ethylene-propylene copolymer rubber phase (B) dispersed within the matrix phase
wherein the heterophasic polypropylene resin has a MFR (2.16 kg, 230° C.) of 1.0 to 100 g/10 min, determined according to ISO 1133, and
a fraction soluble in p-xylene at 25° C. (XCS fraction) which is present in the resin in an amount of 28 to 50 wt %, and which has a molecular weight distribution (M w /M n ) of 1.0 to 4.0, and which has an amount of ethylene comonomer units of 10 to 25 wt %.
2. The heterophasic polypropylene resin according to claim 1 , wherein the matrix phase (A) has a comonomer content of 0.1 to 4.5 wt %, and wherein the comonomer units in matrix phase (A) are selected from a group consisting of alpha-olefins having 2 and/or from 4 to 12 carbon atoms.
3. The heterophasic polypropylene resin according to claim 1 , wherein the XCS fraction has a weight average molecular weight (M w ) of 100 to 350 kg/mol, measured by GPC according to ISO 16014-1 and -4.
4. The heterophasic polypropylene resin according to claim 1 , wherein the XCS fraction has an intrinsic viscosity of 1.0 to 3.0 dl/g, determined according to DIN EN ISO 1628-1 and -3.
5. The heterophasic polypropylene resin according to claim 1 , having a melting temperature (T m ) of 130 to 150° C.
6. The heterophasic polypropylene resin according to claim 1 , having a crystallisation temperature (T c ) of 90 to 120° C.
7. The heterophasic polypropylene resin according to claim 1 , having a tensile modulus of 150 to 500 MPa and an elongation at break of 400 to 700%, determined according to ISO 527-2.
8. The heterophasic polypropylene resin according to claim 1 , having a Charpy notched impact strength at 23° C. of 50 to 150 kJ/m 2 and a Charpy notched impact strength at −20° C. of 30 to 150 kJ/m 2 , determined according to ISO 179-1/1 eA.
9. The heterophasic polypropylene resin according to claim 1 , withstanding a maximum instrumented falling weight force at −20° C. of 1000 to 5000 N, determined according to ISO 6603-2.
10. The heterophasic polypropylene resin according to claim 1 , obtained by a catalyst system comprising an asymmetric catalyst wherein the catalyst system has a porosity of less than 1.40 ml/g.
11. An article comprising the heterophasic polypropylene resin comprising
a propylene random copolymer matrix phase (A), and
an ethylene-propylene copolymer rubber phase (B) dispersed within the matrix phase
wherein the heterophasic polypropylene resin has a MFR (2.16 kg. 230° C.)of 1.0 to 100 g/10 min, determined according to ISO 1133, and a fraction soluble in p-xylene at 25° C. (XCS fraction) which is present in the resin in an amount of 28 to 50 wt %, and which has a molecular weight distribution (M w /M n ) of 1.0 to 4.0, and which has an amount of ethylene comonomer units of 10 to 25 wt %.
12. A power cable having a layer comprising the heterophasic polypropylene resin comprising
a propylene random copolymer matrix phase (A), and
an ethylene-propylene copolymer rubber phase (B) dispersed within the matrix phase
wherein the heterophasic polypropylene resin has a MFR (2.16 kg. 230° C.)of 1.0 to 100 g/10 min, determined according to ISO 1133, and
a fraction soluble in p-xylene at 25° C. (XCS fraction) which is present in the resin in an amount of 28 to 50 wt %, and which has a molecular weight distribution (M w /M n ) of 1.0 to 4.0, and which has an amount of ethylene comonomer units of 10 to 25 wt %.
13. A process for producing the heterophasic polypropylene resin comprising
a propylene random copolymer matrix phase (A), and
an ethylene-propylene copolymer rubber phase (B) dispersed within the matrix phase
wherein the heterophasic polypropylene resin has a MFR (2.16 kg. 230° C.) of 1.0 to 100 g/10 min, determined according to ISO 1133, and
a fraction soluble in p-xylene at 25° C. (XCS fraction) which is present in the resin in an amount of 28 to 50 wt %, and which has a molecular weight distribution (M w /M n ) of 1.0 to 4.0, and which has an amount of ethylene comonomer units of 10 to 25 wt %,
wherein the propylene copolymer matrix phase is prepared in a first stage and the ethylene-propylene copolymer rubber phase (B) is prepared in a second stage in the presence of the first stage product.