View Patent ↗The invention according to the present invention relates to the manufacture of paper and or boards and/or binding agents and a method and apparatus related to the same by providing for the defibrillation of cellulose fibers into a form in which the same can be subsequently sued to form the finished product directly or can be used to bind other materials together and then be formed into the finished product. The apparatus includes a twin screw conveyor through the material and liquid passes to be processed.
1. Method for the treatment of a composition comprising cellulose fibres into a composition comprising cellulose microfibers characterized in that the method comprises the steps of:
a) Providing a composition comprising cellulose fibres;
b) Admixing aqueous solvent to said composition comprising cellulose fibres to provide a pulp suspension comprising cellulose fibres;
c) Feeding said pulp suspension comprising cellulose fibres into a refining step comprising a mechanical fibrillation process executed using a refining co-rotating twin screw;
d) Refining said pulp suspension comprising cellulose fibres with at least the use of said refining twin screw, to provide a composition comprising cellulose microfibers; and wherein said obtained composition comprising relined cellulose fibres at the end of the refining step, can be formed into a range of papers, boards, and further wherein the composition comprising refined cellulose fibres has a Schopper-Riegler value (SR) upon leaving the twin-screw of step c), of at least 35 SR.
2. Method according to claim 1 wherein in step b) a pulp suspension is provided with a consistency of at least 30%, preferably between, and including 40% and 60%.
3. Method according to claim 1 wherein the composition comprising refined cellulose fibres has a Schopper-Riegler value (SR) upon leaving the twin-screw of step c), of at least between −35 and 75 SR.
4. Method according to claim 1 wherein the composition comprising cellulose fibres of step a) is selected from the group consisting of paper, waste paper, recycled paper and pulps made from, but not confined to, softwoods, hardwoods, hemp, flax, cotton linters, abaca, wood waste, cereal straws, bagasse and bamboo.
5. Method according to claim 1 wherein the refining twin screw is a co-rotating or counter rotating twin screw unit.
6. Method according to claim 1 wherein said composition comprising refined cellulose fibres is formed into a 2 dimensional shapes.