Non-aqueous secondary battery
View Patent ↗The non-aqueous secondary battery of the present invention includes a positive electrode, a negative electrode, a non-aqueous electrolyte, and a separator, the negative electrode contains a negative electrode active material containing a graphitic carbon material and a composite in which a carbon coating layer is formed on a surface of a core material containing Si and O as constituent elements, the composite has a carbon content of 10 to 30 mass %, the composite has an intensity ratio I 510 /I 1343 of a peak intensity I 510 at 510 cm −1 derived from Si to a peak intensity I 1343 at 1343 cm −1 derived from carbon of 0.25 or less when a Raman spectrum of the composite is measured at a laser wavelength of 532 nm, and the half-width of the (111) diffraction peak of Si is less than 3.0° when the crystallite size of an Si phase contained in the core material is measured by X-ray diffractometry using CuKα radiation.
1. A non-aqueous secondary battery comprising a positive electrode, a negative electrode, a non-aqueous electrolyte, and a separator,
the negative electrode comprising a negative electrode active material comprising a graphitic carbon material and a composite in which a carbon coating layer is formed on a surface of a core material comprising Si and O as constituent elements,
the composite having a carbon content of 10 to 30 mass %,
the composite having an intensity ratio I 510 /I 1343 of a peak intensity I 510 at 510 cm −1 derived from Si to a peak intensity I 1343 at 1343 cm −1 derived from carbon of 0.25 or less when a Raman spectrum of the composite is measured at a laser wavelength of 532 nm, and
a half-width of a (111) diffraction peak of Si being less than 3.0° when a crystallite size of an Si phase contained in the core material is measured by X-ray diffractometry using CuKα radiation.
2. The non-aqueous secondary battery according to claim 1 , wherein the half-width of a (111) diffraction peak of Si is 2.5° or less.
3. The non-aqueous secondary battery according to claim 1 , wherein the half-width of a (111) diffraction peak of Si is 0.5° or greater.
4. The non-aqueous secondary battery according to claim 1 , wherein the coating layer of the composite is a layer formed by thermal decomposition when hydrocarbon-based gas is heated in a gaseous phase.
5. The non-aqueous secondary battery according to claim 1 , wherein the material comprising Si and O as constituent elements is represented by a general compositional formula SiO x where x is 0.5≦x≦1.5.
6. The non-aqueous secondary battery according to claim 1 , wherein the negative electrode active material has the composite content of 0.01 mass % or greater and 20 mass % or less relative to the entire negative electrode active material.
7. The non-aqueous secondary battery according to claim 1 , wherein the composite has an average particle diameter of 0.5 to 20 μm.
8. The non-aqueous secondary battery according to claim 1 , wherein P/N is 1.0 to 3.6, with P being mass of the positive electrode active material of the positive electrode and N being mass of the negative electrode active material of the negative electrode.
9. The non-aqueous secondary battery according to claim 1 , wherein the separator is a laminated separator composed of a porous layer containing 50 volume % or greater of a resin that melts when a temperature reaches a melting point or higher and a porous layer containing 50 volume % or greater of an inorganic filler having an upper temperature limit of 150° or higher.
10. The non-aqueous secondary battery according to claim 1 , wherein the non-aqueous electrolyte comprises a cyclic fluorinated carbonate.
11. A non-aqueous secondary battery comprising a positive electrode, a negative electrode, a non-aqueous electrolyte, and a separator,
the negative electrode comprising a negative electrode active material comprising a graphitic carbon material and a composite in which a carbon coating layer is formed on a surface of a core material comprising Si and O as constituent elements,
the composite having a carbon content of 10 to 30 mass %,
the composite having an intensity ratio I 510 /I 1343 of a peak intensity I 510 at 510 cm −1 derived from Si to a peak intensity I 1343 at 1343 cm −1 derived from carbon of 0.25 or less when a Raman spectrum of the composite is measured at a laser wavelength of 532 nm,
a half-width of a (111) diffraction peak of Si being less than 3.0° when a crystallite size of an Si phase contained in the core material is measured by X-ray diffractometry using, CuKα radiation,
the separator being a laminated separator composed of a porous layer containing 50 volume % or greater of a resin that melts when a temperature reaches a melting point or higher and a porous layer containing 50 volume % or greater of an inorganic filler having an upper temperature limit of 150° C. or higher, and
the negative electrode active material having a composite content of 0.01 mass % or greater and 20 mass % or less relative to an entire negative electrode active material, and
the non-aqueous electrolyte comprising a cyclic fluorinated carbonate.
12. The non-aqueous secondary battery according to claim 11 , wherein the half-width of a (111) diffraction peak of Si is 2.5° or less.
13. The non-aqueous secondary battery according to claim 11 , wherein the half-width of a (111) diffraction peak of Si is 0.5° or greater.
14. The non-aqueous secondary battery according to claim 11 , wherein the coating layer of the composite is a layer formed by thermal decomposition when hydrocarbon-based gas is heated in a gaseous phase.
15. The non-aqueous secondary battery according to claim 11 , wherein the material comprising Si and O as constituent elements is represented by a general compositional formula SiO x where x is 0.5≦x≦1.5.
16. The non-aqueous secondary battery according to claim 11 , wherein the composite has an average particle diameter of 0.5 to 20 μm.
17. The non-aqueous secondary battery according to claim 11 , wherein P/N is 1.0 to 3.6, with P being mass of the positive electrode active material of the positive electrode and N being mass of the negative electrode active material of the negative electrode.