Vapor permeable barrier coating applicable at low temperature
View Patent ↗Disclosed is a coating composition that includes an aqueous emulsion of a hydrophobic acrylic polymer, a water-soluble polymer, and an inorganic filler, and further includes a freezing-point lowering component to permit low temperature application. The freezing-point lowering component will preferably include a water-soluble, corrosion inhibiting salt. The coating composition will also optionally and preferably include an evaporation enhancing component to promote faster drying and skin formation at low temperatures. The coating composition may be coated onto a construction surface (e.g., by spraying) where, after drying, it will form a fully adhered barrier membrane that is water-vapor permeable, but air and liquid-water impermeable. Such membrane will preferably have sufficient coating thickness and sufficiently high elongation that it will bridge joints and cracks.
1. A liquid coating composition useful for providing a water-vapor permeable, air barrier membrane by coating on a construction surface, the liquid coating composition being an aqueous emulsion, comprising:
a hydrophobic acrylic polymer, wherein the hydrophobic acrylic polymer comprises about 50% to 97% by weight based on total solids in the liquid composition, the hydrophobic acrylic polymer comprising a homopolymer or a copolymer of an acrylic ester having a repeating group represented by the structure —(—CH 2 —C(R 1 )HCOOR—)— wherein R is a C2-C8 alkyl group and R 1 is H or CH 3 ;
a water soluble polymer, wherein the water-soluble polymer comprises about 1% to 20% by weight based on total solids in the liquid composition, and wherein the water-soluble polymer comprises polyvinyl alcohol, polyethylene oxide, water soluble cellulosic polymers, hydrolyzed maleic anhydride polymers and copolymers, polyvinylpyrrolidone, sulfonated polystyrene, polysulfoethyl acrylate, poly(2-hydroxyethylacrylate), polyacrylamide, poly(acrylic acid) and alkali metal salts thereof, natural or synthetically modified polysaccharides, proteins, alginates, xanthan gums, or guar gums, or combinations of two or more of such water soluble polymers;
an inorganic filler, wherein the inorganic filler comprises about 2-40% by weight based on total solids in the liquid composition;
a freezing-point lowering component comprising a water-soluble metal salt, wherein the water-soluble metal salt comprises about 0.5-15% by weight of the total weight of the liquid composition, said water-soluble metal salt comprising calcium nitrite, sodium nitrite, or a mixture thereof; and
an evaporation enhancing agent in an amount of about 0.5-15% by weight of the total weight of the liquid composition, the evaporation enhancing agent comprising at least one solvent selected from methanol, ethanol, oxybis-propanol, vinyl acetate, butyl acetate, ethyl acetate, methyl isobutyl ketone, methyl ethyl ketone, or a combination of two or more of these solvents; and
wherein the liquid composition comprises water in an amount of about 30-50% by weight of the total weight of the liquid composition.
2. The composition of claim 1 wherein the water-soluble metal salt further comprises a water-soluble, alkali, alkaline earth or rare earth metal chloride salt nitrate, or a combination of two or more of these salts.
3. The composition of claim 1 wherein the water-soluble metal salt further comprises sodium chloride, potassium chloride, calcium chloride, magnesium chloride, calcium nitrate, cerium chloride, cerium nitrate, calcium magnesium acetate, potassium formate, or sodium silicate, or a combination of two or more of these salts.
4. The composition of claim 1 wherein the evaporation enhancing agent comprises ethanol.
5. The composition of claim 1 wherein the evaporation enhancing agent comprises a volatile organic solvent.
6. The composition of claim 1 wherein the evaporation enhancing agent comprises a volatile organic solvent that forms an azeotrope with water.
7. The composition of claim 1 wherein the hydrophobic acrylic polymer comprises a copolymer of butyl acrylate and styrene.
8. The composition of claim 7 wherein the water soluble polymer comprises polyvinyl alcohol.
9. A liquid coating composition useful for providing a water-vapor permeable, air barrier membrane by coating on a construction surface, the liquid coating composition being an aqueous emulsion, comprising:
a hydrophobic acrylic polymer, wherein the hydrophobic acrylic polymer comprises about 50% to 97% by weight based on total solids in the liquid composition;
a water soluble polymer, wherein the water-soluble polymer comprises about 1% to 20% by weight based on total solids in the liquid composition, and wherein the water-soluble polymer comprises polyvinyl alcohol, polyethylene oxide, water soluble cellulosic polymers, hydrolyzed maleic anhydride polymers and copolymers, polyvinylpyrrolidone, sulfonated polystyrene, polysulfoethyl acrylate, poly(2-hydroxyethylacrylate), polyacrylamide, poly(acrylic acid) and alkali metal salts thereof, natural or synthetically modified polysaccharides, proteins, alginates, xanthan gums, or guar gums, or combinations of two or more of such water soluble polymers;
an inorganic filler, wherein the inorganic filler comprises about 2-40% by weight based on total solids in the liquid composition;
a freezing-point lowering component comprising a water-soluble metal salt, wherein the water-soluble metal salt comprises about 0.5-15% by weight of the total weight of the liquid composition, said water-soluble metal salt comprising calcium nitrite, sodium nitrite, or a mixture thereof; and
an evaporation enhancing agent in an amount of about 0.5-15% by weight of the total weight of the liquid composition, the evaporation enhancing agent comprising at least one solvent selected from methanol, ethanol, oxybis-propanol, vinyl acetate, butyl acetate, ethyl acetate, methyl isobutyl ketone, methyl ethyl ketone, or a combination of two or more of these solvents; and
wherein the liquid composition comprises water in an amount of about 30-50% by weight of the total weight of the liquid composition.
10. The composition of claim 9 wherein the evaporation enhancing agent comprises ethanol.
11. The composition of claim 9 wherein the hydrophobic acrylic polymer comprises a homopolymer or a copolymer of an acrylic ester having a repeating group represented by the structure —(—CH 2 —C(R 1 )HCOOR—)— wherein R is a C2-C8 alkyl group and R1 is H or CH 3 .
12. The composition of claim 9 wherein the evaporation enhancing agent comprises a volatile organic solvent that forms an azeotrope with water.