Polyolefin composition for an interior sheet/film
View Patent ↗The present invention relates to a polyolefin composition for an interior sheet/film. The polyolefin composition of the present invention for an interior sheet comprises 70 to 99 wt % of polyolefin and 1 to 30 wt % of modified polyethylene terephthalate having a melting point of 130 to 180° C. The polyolefin composition of the present invention is environmentally friendly and has good physical properties such as workability, printing characteristics, and adhesiveness. In addition, sheets having various thicknesses can be produced by extrusion without having to stretch the sheets, and thus the sheets can be used separately or in combination in various application fields.
1. A polyolefin composition for an interior sheet/film, comprising 70˜99 wt % of polyolefin and 1˜30 wt % of modified polyethylene terephthalate having a melting point of 130˜180° C.
2. The polyolefin composition of claim 1 , wherein the polyolefin is polypropylene or polypropylene containing 2˜30 wt % of an elastic ethylene-propylene copolymer.
3. The polyolefin composition of claim 1 , wherein the polyolefin is a mixture comprising 50˜99 wt % of polypropylene or polypropylene containing 2˜30 wt % of an elastic ethylene-propylene copolymer, and 1˜50 wt % of at least one polyethylene selected from the group consisting of low-density polyethylene, linear low-density polyethylene and high-density polyethylene.
4. The polyolefin composition of claim 1 , wherein the modified polyethylene terephthalate is polyethylene succinic terephthalate or polyethylene adipic terephthalate.
5. The polyolefin composition of claim 1 , further comprising 0.1˜40 wt % of at least one inorganic material selected from the group consisting of calcium carbonate, talc, mica and zeolite.
6. The polyolefin composition of claim 1 , further comprising 1˜30 wt % of at least one rubber component selected from the group consisting of ethylenevinyl acetate (EVA), ethylene/propylene/non-conjugated diene terpolymer (EPDM), styrene-butadiene rubber (SBR), and acrylonitrile-butadiene synthetic rubber (NBR).
7. The polyolefin composition of claim 1 , further comprising 0.001˜3 wt % of at least one compatibilizer selected from the group consisting of EVA, methylmethacrylate-butadiene-styrene (MBS), maleic anhydride, and polypropylene-graft-maleic anhydride (PP-g-MA).