View Patent ↗A crosslinked coating composition formed from polyurethane polyols and blocked or unblocked polyisocyanates. The polyisocyanates, in particular, comprise at least bis(isocyanatomethyl)cyclohexane. The coating is substantially free from ester functionality that forms a contiguous part of the network backbone. A clearcoat formed from the described components and having a majority of urethane bonds is very resistant to environmental etch damage.
1. A coating composition comprising a crosslinkable component and a crosslinking component wherein the crosslinkable component comprises:
(i) a polyurethane polyol;
(ii) a silane resin;
(iii) a silsesquioxane; and
wherein the crosslinking component is selected from the group consisting of bis(isocyanatomethyl)cyclohexane, an oligomer of bis(isocyanatomethyl)cyclohexane and a combination thereof wherein the coating composition is a clearcoat composition.
2. The coating composition of claim 1 wherein said crosslinking component further comprises melamines.
3. The coating composition of claim 1 wherein the crosslinkable component comprises in the range of from 10 to 55 percent by weight of the polyurethane polyol, in the range of from 20 to 80 percent by weight silane resin, and in the range of from 10 to 70 percent by weight silsesquioxane, wherein the percents by weight are based on the total amount of crosslinkable component.
4. The coating composition of claim 1 wherein the isocyanate groups are blocked with a blocking agent and said blocking agents are selected from the group consisting of alcohols, phenols, oximes, heterocyclic compounds and a combination thereof.
5. The coating composition of claim 1 wherein the polyurethane polyol is the product of a branched polyester polyol and a polyisocyanate.
6. The coating composition of claim 5 wherein the branched polyester polyol is the reaction product of;
a) in the range of from 20 to 80 percent by weight of one or more monofunctional carboxylic acid monomers having 2 to 17 carbon atoms;
b) in the range of from 10 to 40 percent by weight of one or more hydroxyl functional monomers having a hydroxyl functionality of 3 to 10; and
c) in the range of from 10 to 40 percent by weight of one or more polycarboxylic acid monomers; and
wherein all percentages by weight are based on the total amount of monomers used to make the branched polyester polyol.
7. A method of coating a substrate said method comprising the steps of;
1) applying a layer of a coating composition to the substrate; and
2) curing the applied coating composition;
wherein said coating composition comprises a crosslinkable component and a crosslinking component, and wherein the crosslinkable component comprises:
(i) a silane resin;
(ii) a silsesquioxane;
(iii) a polyurethane polyol; and
wherein the crosslinking component comprises a crosslinking agent selected from the group consisting of bis(isocyanatomethyl)cyclohexane, an oligomer of bis(isocyanatomethyl)cyclohexane and a combination thereof.
8. The method of claim 7 wherein the crosslinking component further comprises melamines.
9. The method of claim 7 wherein the crosslinkable component comprises in the range of from 10 to 55 percent by weight of the polyurethane polyol, in the range of from 20 to 80 percent by weight silane resin, and in the range of from 10 to 70 percent by weight silsesquioxane, wherein the percents by weight are based on the total amount of crosslinkable component.
10. The method of claim 7 wherein the isocyanate groups are blocked with a blocking agent and said blocking agents are selected from the group consisting of alcohols, phenols, oximes, heterocyclic compounds and a combination thereof.
11. The method of claim 7 wherein the polyurethane polyol is the product of a branched polyester polyol and a polyisocyanate.
12. The method of claim 7 wherein the branched polyester polyol is the reaction product of;
a) in the range of from 20 to 80 percent by weight of one or more monofunctional carboxylic acid monomers having 2 to 17 carbon atoms;
b) in the range of from 10 to 40 percent by weight of one or more hydroxyl functional monomers having a hydroxyl functionality of 3 to 10; and
c) in the range of from 10 to 40 percent by weight of one or more polycarboxylic acid monomers; and
wherein all percentages by weight are based on the total amount of monomers used to make the branched polyester polyol.
13. A substrate coated by a layer of a dried and cured coating composition wherein the coating composition comprises a crosslinkable component and a crosslinking component wherein the crosslinkable component comprises:
(i) a polyurethane polyol;
(ii) a silane resin;
(iii) a silsesquioxane; and
wherein the crosslinking component comprises a crosslinking agent selected from the group consisting of bis(isocyanatomethyl)cyclohexane, an oligomer of bis(isocyanatomethyl)cyclohexane and a combination thereof.
14. The substrate of claim 13 wherein the crosslinkable component comprises is the range of from 10 to 55 percent of the polyurethane polyol, in the range of from 20 to 80 percent silane resin, and in the range of from 10 to 70 percent silsesquioxane.
15. The substrate of claim 13 wherein the crosslinking component further comprises melamines.
16. The substrate of claim 13 wherein the isocyanate groups are blocked with a blocking agent and said blocking agents are selected from the group consisting of alcohols, phenols, oximes, heterocyclic compounds and a combination thereof.
17. The substrate of claim 13 wherein the polyurethane polyol is the product of a branched polyester polyol and a polyisocyanate.
18. The substrate of claim 17 wherein the branched polyester polyol is the reaction product of;
a) in the range of from 20 to 80 percent by weight of one or more monofunctional carboxylic acid monomers having 2 to 17 carbon atoms;
b) in the range of from 10 to 40 percent by weight of one or more hydroxyl functional monomers having a hydroxyl functionality of 3 to 10; and
c) in the range of from 10 to 40 percent weight of one or more polycarboxylic acid monomers; and
wherein all percentages by weight are based on the total amount of monomers used to make the branched polyester polyol.