Flame-proofed polymer compositions
View Patent ↗The invention relates to a flame-proofed polymer composition that can be obtained form one or more α-olefin-vinyl acetate copolymers, having a vinyl acetate content of 40 to 90 wt %, relative to the total weight of the α-olefin vinyl acetate copolymers, and from a synergistic flame-proofing material combination, comprising, as component A, a phosphinic acid salt of the formula (I), where R 1 , R 2 are C 1 -C 6 -alkyl, preferably C 1 -C 4 -alkyl, linear or branched; M is calcium, aluminum, zinc ions; m is 2 or 3; and, as component B, a metal hydroxide, preferably aluminum hydroxide (ATH).
1. A flameproofed polymer composition comprising:
one or more α-olefin/vinyl acetate copolymers having a vinyl acetate content of 40 to 90% by weight based on the total weight of the α-olefin/vinyl acetate copolymer, and a Melt Flow Index value of more than 1 to 40 g/10 min per ISO 1133, and
a flameproofing combination comprising:
10 to 90 phr of a phosphinic acid salt of the formula (I)
in which
R 1 , R 2 denotes C 1 -C 6 -alkyl, linear or branched;
M denotes calcium, aluminium or zinc ions;
m denotes 2 or 3, and
100 to 190 phr of a metal hydroxide, and
wherein the composition is halogen-free.
2. The flameproofed polymer composition according to claim 1 , wherein the phosphinic acid salt is an aluminium phosphinate.
3. The flameproofed polymer composition according to claim 1 , wherein the total amount of flameproofing combination is between 110 phr and 280 phr.
4. The flameproofed composition according to claim 1 , wherein the flameproofing combination comprises 160 phr of aluminium hydroxide and 30 phr of aluminium phosphinate.
5. The flameproofed composition according to claim 1 , having an LOI of at least 35% and a hardness of not more than 90 Shore A.
6. A flameproofing combination for the preparation of a flameproofed polymer composition comprising one or more α-olefin/vinyl acetate copolymers having a vinyl acetate content of 50 to 80% by weight based on the total weight of the α-olefin/vinyl acetate copolymer, and a Melt Flow Index value of more than 1 to 40 g/10 min per ISO 1133, 10 to 90 phr of aluminium phosphinate, and 100 to 190 phr of a metal hydroxide, wherein the composition is halogen-free.
7. The flameproofing combination according to claim 6 , comprising 160 phr of aluminum hydroxide and 30 phr of aluminium phosphinate.
8. A process to treat plastics, rubbers, thermoplastic elastomers or thermoplastic vulcanizates, the process comprising adding a flameproofing combination according to claim 1 in the production of the plastic, rubber, thermoplastic elastomer or thermoplastic vulcanizate.
9. A process for the treatment of a cable, plastic molding material, resilient molding material, electrical coated conductors, adhesive, or floor covering, the process comprising adding a flame proofing combination according to claim 1 in the production of the cable, plastic molding material, resilient molding material, electrical coated conductor, adhesive, or floor covering.