Method for manufacturing a lithium complex metal oxide
A method for producing a lithium mixed metal oxide, which includes mixing a lithium compound, metallic Ni or a compound thereof, and one or more transition metals selected from the group consisting of Mn, Co, Ti, Cr and Fe or a compound thereof; and calcining the obtained raw material mixture under an atmosphere of the concentration of carbon dioxide of from 1% by volume to 15% by volume at 630° C. or higher.
1. A method for producing a lithium mixed metal oxide, the method comprising:
mixing a lithium compound, metallic Ni or a compound thereof, and one or more transition metals selected from the group consisting of Mn, Co, Ti, Cr and Fe or a compound thereof to obtain a raw material mixture; and
calcining the raw material mixture under an atmosphere having a concentration of carbon dioxide of from 1% by volume to 15% by volume at 630° C. or higher,
wherein the raw material mixture contains a reaction accelerator made of one or more compounds selected from the group consisting of a carbonate, a sulfate and a chloride of one or more elements selected from the group consisting of Na, K, Rb, Cs, Ca, Mg, Sr and Ba.
2. The method for producing a lithium mixed metal oxide according to claim 1 , wherein the concentration of oxygen in the calcining step is from 1% by volume to 50% by volume.
3. The method for producing a lithium mixed metal oxide according to claim 1 , wherein the calcination time at 630° C. or higher is from 0.5 hours to 24 hours.
4. The method for producing a lithium mixed metal oxide according to claim 1 , further comprising:
a retention step at a temperature which is 30° C. or more lower than a calcination temperature and is 600° C. or higher.
5. The method for producing a lithium mixed metal oxide according to claim 1 , wherein the transition metal is Mn and/or Fe.
6. The method for producing a lithium mixed metal oxide according to claim 1 , wherein calcination is performed by a gas furnace using flame of a combustion gas as a heat source.
7. The method for producing a lithium mixed metal oxide according to claim 1 , wherein the transition metals are Mn and Fe, and the reaction accelerator is a carbonate.