Reverse osmosis composite membranes for boron removal
View Patent ↗Improved methods for reducing boron concentration in seawater or brackish water, while simultaneously maintaining or improving the salt rejection of membrane and flow performance of polyamide reverse osmosis (RO) membranes include contacting the water with a composite membrane comprising moieties derived from an aromatic sulfonyl halide, a heteroaromatic sulfonyl halide, a sulfinyl halide; a sulfenyl halide; a sulfuryl halide; a phosphoryl halide; a phosphonyl halide; a phosphinyl halide; a thiophosphoryl halide; a thiophosphonyl halide, an isocyanate, a urea, a cyanate, an aromatic carbonyl halide, an epoxide or a mixture thereof.
1. A method for preparing a composite polyamide membrane comprising
contacting under interfacial polymerization conditions an organic solution comprising trimesoyl chloride with an aqueous solution comprising phenylene diamine to form a composite polyamide membrane, said contacting being carried out on a surface of a porous base membrane, said organic solution further comprising cyclohexanone and an aryl sulfonyl halide selected from 1,3-benzenedisulfonyl chloride and 1,3,6-naphthalenetrisulfonyl chloride; and
concentration of the aryl sulfonyl halide in the aqueous solution ranging from about 0.18% to about 0.71% by weight; and
contacting the composite polyamide membrane with a sodium hypochlorite solution to form a treated composite polyamide membrane having salt passage less than or equal to 1.26% and A-value greater than or equal to 16.5.
2. A method according to claim 1 , wherein the concentration of free chlorine in the sodium hypochlorite solution ranges from about 10 ppm to about 4000 ppm.
3. A method according to claim 1 , wherein the aryl sulfonyl halide is 1,3,6-naphthalenetrisulfonyl chloride.
4. A method according to claim 1 , wherein the aryl sulfonyl halide is 1,3-benzenedisulfonyl chloride.
5. A composite membrane prepared by the method of claim 1 .