Process to recycle end of life CDTE modules and manufacturing scrap
A method for recycling of thin film Cadmium Telluride photovoltaic modules at the end of their life, and manufacturing scrap, has been developed. This method allows for minimum glass fine generation, requires little or no acid compared to other methods, and generates a pure cadmium and tellurium product at recoveries in excess of about 80 percent. In addition, the process allows for the recovery of a clean soda-lime plate glass product.
1. A method of recycling coated substrates, comprising:
subjecting a substrate comprising a thin film to an oxidation in an oxygen containing environment to produced an oxidized thin film;
subjecting the oxidized thin film to an alkaline leach to produce a solid containing cadmium and a solution containing tellurium; and
recovering tellurium from the solution containing tellurium.
2. The method of claim 1 , wherein the recovering tellurium comprises electrowinning the solution containing tellurium.
3. The method of claim 2 , wherein a current density is about 25 mA/cm2 in the electrowinning.
4. The method of claim 2 , wherein the current density is between about 20 mA/cm2 and about 30 mA/cm2.
5. The method of claim 1 , further comprising recovering cadmium from the solid containing cadmium.
6. The method of claim 5 , wherein the recovering cadmium further comprises:
subjecting the solid containing cadmium to an acid solution to produce a solution containing cadmium; and
electrowinning the solution containing cadmium.
7. The method of claim 1 , wherein the oxidation occurs at a temperature of between about 650° C. and about 750° C.
8. The method of claim 1 , wherein a pulp density of the alkaline leach is between 10 g/L and 300 g/L.
9. The method of claim 1 , wherein a leaching solution of the alkaline leach is NaOH.
10. A method of recycling a photovoltaic module comprising a substrate, a coating, and a secondary substrate, the method comprising:
subjecting the photovoltaic module to delamination to remove the secondary substrate;
subjecting the photovoltaic module to an oxidation in an oxygen containing environment to produced an oxidized coating;
subjecting the oxidized coating to an alkaline leach to produce a solid containing cadmium and a solution containing tellurium; and
recovering tellurium from the solution containing tellurium.
11. The method of claim 10 , further comprising:
following the delamination step, media blasting the photovoltaic module and removing the substrate.
12. The method of claim 10 , wherein the recovering tellurium comprises electrowinning the solution containing tellurium.
13. The method of claim 12 , wherein a current density is about 25 mA/cm2 in the electrowinning.
14. The method of claim 10 , further comprising recovering cadmium from the solid containing cadmium.
15. The method of claim 14 , wherein the recovering cadmium further comprises:
subjecting the solid containing cadmium to an acid solution to produce a solution containing cadmium; and
electrowinning the solution containing cadmium.
16. The method of claim 10 , wherein the alkaline leach further comprises abrasion stripping.
17. The method of claim 10 , further comprising subjecting the oxidized coating to comminution.
18. The method of claim 10 , wherein the alkaline leach further comprises attrition scrubbing.
19. A method of recycling a photovoltaic module, comprising:
subjecting the photovoltaic module to a delamination in a nitrogen furnace, wherein the photovoltaic module comprises a secondary substrate and a coated substrate;
removing a secondary substrate from the coated substrate;
subjecting the coated substrate to a media blast until a thin film is recovered;
subjecting the thin film to an oxidation in an oxygen containing atmosphere furnace to produced an oxidized thin film;
leaching the oxidized thin film in an alkaline leach to produce a sludge containing cadmium and a solution containing tellurium;
recovering cadmium from the sludge containing cadmium to produce a cadmium product;
electrowinning the solution containing tellurium to produce a tellurium product;
recovering the alkaline leach; and
recycling the recovered alkaline leach to the leaching step.
20. The method of claim 19 , wherein the recovered alkaline leach is combined with new alkaline leach, and wherein the new alkaline leach is NaOH.