Platinum monolayer for fuel cell

1. A fuel cell electrode forming method, comprising:

providing a gas diffusion layer;

providing a catalyst core layer, the catalyst core layer supported by the gas diffusion layer;

supporting the gas diffusion layer between an electrochemical cell and a plate, the plate having channels for circulating a platinum solution;

depositing a copper monolayer on the catalyst core layer;

covering at least a portion of the copper monolayer supported by the gas diffusion layer of the fuel cell electrode with the platinum solution; and

replacing the copper monolayer to form a platinum monolayer from the platinum solution by exposing the copper monolayer to the platinum solution while forcing the platinum solution through the gas diffusion layer with a pump.

2. The fuel cell electrode forming method of claim 1 , including press fitting a membrane to the platinum monolayer.

3. The fuel cell electrode forming method of claim 2 , wherein the membrane comprises a polymer electrolyte membrane.

4. The fuel cell electrode forming method of claim 1 , wherein the platinum monolayer is at least one atom thick.

5. The fuel cell electrode forming method of claim 1 , wherein the copper monolayer is one atom thick.

6. The fuel cell electrode forming method of claim 1 , including coating the gas diffusion layer with a core material to form the catalyst core layer.

7. The fuel cell electrode forming method of claim 1 , wherein the gas diffusion layer is a carbon paper.

8. The fuel cell electrode forming method of claim 7 , wherein the carbon paper is hydrophilicity or hydrophobilicity treated.

9. The fuel cell electrode forming method of claim 1 , wherein the gas diffusion layer has a bilayer.

10. The fuel cell electrode forming method of claim 1 , wherein the catalyst core layer comprises at least one of palladium, platinum, gold, ruthenium, rhodium, iridium, osmium, rhenium, silver, and their alloys.

11. The fuel cell electrode forming method of claim 6 , wherein the core material is mixed with a proton conductive ionomer.

12. A method for forming a fuel cell electrode in an electrochemical cell, the method comprising:

providing a gas diffusion layer;

providing a catalyst core layer, the catalyst core layer supported by the gas diffusion layer;

positioning the gas diffusion layer between the electrochemical cell and a plate, the plate having channels for circulating a platinum solution;

depositing a copper monolayer on the catalyst core layer;

covering at least a portion of the copper monolayer supported by the gas diffusion layer of the fuel cell electrode with the platinum solution, the electrochemical cell containing the platinum solution; and

replacing the copper monolayer to form a platinum monolayer from the platinum solution, the replacing including exposing the copper monolayer to the platinum solution while forcing the platinum solution through the gas diffusion layer.

13. The method of claim 12 , further comprising pressing the copper monolayer and the catalyst core layer against a copper solution.

14. The method of claim 12 , wherein forcing the platinum solution through the gas diffusion layer includes forcing the platinum solution through the gas diffusion layer with the assistance of channels provided in the plate supporting the gas diffusion layer.