Method of controlling scale in steam generating systems
View Patent ↗Water soluble or water dispersible terpolymers are employed in high pressure steam generating systems to control deposit formation and contaminant transport in the aqueous medium in such systems. The terpolymer may comprise repeat units formed from acrylic acid, allylalkoxylated ethers, and allylhydroxylated alkyl ether.
1. A method of controlling deposit formation on the structural parts of a steam generating system exposed to an aqueous medium under steam generating conditions, said steam generating system operating under a pressure of 600 psig and greater, said method comprising adding to said aqueous medium an effective amount of a terpolymer having the structure
wherein E is the repeat unit remaining after polymerization of an ethylenically unsaturated with compound; R 1 is H or C 1 -C 4 alkyl; R 2 is ethylene, isopropylene, or propylene; f is an integer of 1-100; A is OSO 3 or SO 3 ; G is selected from H or a cation including Na, K, or NH 4 ; R 3 is H or C 1 -C 4 with alkyl; and R 4 is a hydroxyl substituted alkylene radical having from 1 to about 6 carbon atoms; c, d, and e are each a positive integer, and wherein X is OSO 3 or SO 3 and Z is Na, K, NH 4 or H.
2. A method as recited in claim 1 wherein E is acrylic acid or salt thereof, R 1 is H, and R 2 is —(—CH 2 —CH 2 )—, X is OSO − 3 ; R 3 is H, R 4 is 2-hydroxypropyl; A is SO 3 and G is H or a cation including Na, K, or NH4.
3. A method as recited in claim 2 wherein said terpolymer is added to said aqueous medium in an amount of between about 0.1 to 500 ppm.
4. A method as recited in claim 2 wherein said terpolymer is added to said aqueous medium in an amount of between about 2 to 100 ppm.
5. A method as recited in claim 1 wherein said steam generating system is operating under a pressure of about 900 psig or greater.
6. A method as recited in claim 1 wherein said deposit formation comprises deposit forming species selected from Ca, Mg, Fe, and silica.
7. A method as recited in claim 1 wherein said aqueous medium comprises Fe, said method being effective to maintain said Fe dispersed in said aqueous medium during steam generation.
8. A method of controlling deposit formation in an aqueous medium of a steam generating system, said deposit formation being of the type resulting from the presence of Ca, Mg, Fe, or silica in said aqueous medium and said steam generating system being operated at pressure of 600 psig and greater, said method comprising adding to said aqueous medium a water soluble or water dispersible terpolymer of i) acrylic acid or soluble salt thereof; ii) allylalkoxylated ether or water soluble salt thereof; and iii) allylhydroxylated alkyl sulfonate ether or water soluble salt thereof, wherein ii) is allylethoxysulfate.
9. A method as recited in claim 8 wherein ii) is allylethoxy (10) sulfate.
10. A method as recited in claim 8 wherein iii) is allyl-2-hydroxypropyl sulfonate ether.
11. A method as recited in claim 8 wherein said steam generating system is operated at pressure of about 900 psig or greater.
12. A method as recited in claim 8 wherein said aqueous medium comprises Fe, said method being effective to maintain said Fe dispersed in said aqueous medium during steam generation.
13. A method as recited in claim 8 wherein said aqueous medium comprises Ca, Mg, and silica.
14. A method as recited in claim 1 wherein said pressure is between 600 and 1500 psig.
15. A method as recited in claim 1 wherein said pressure is between 600 and 900 psig.
16. A method as recited in claim 8 wherein said pressure is between 600 and 1500 psig.
17. A method as recited in claim 8 wherein said pressure is between 600 and 900 psig.