Method for manufacturing seamless steel pipe for line pipe and seamless steel pipe for line pipe
View Patent ↗There is provided a method for manufacturing a seamless steel pipe for line pipe, capable of improving the toughness of the seamless steel pipe for line pipe. A round billet having a chemical composition, by mass percent, of C: 0.02 to 0.15%, Si: at most 0.5%, and Mn: 0.5 to 2.5%, the balance being Fe and impurities, is heated. The heated round billet is piercing-rolled to produce a hollow shell. The hollow shell is elongated and rolled and sized to produce a seamless steel pipe. The seamless steel pipe is water cooled, and the water cooling is stopped when the temperature of the seamless steel pipe reaches at most 450° C. The water-cooled seamless steel pipe is quenched, and the quenched seamless steel pipe is tempered.
1. A method for manufacturing a seamless steel pipe for line pipe, comprising the steps of:
heating a round billet having a chemical composition comprising, by mass percent, C: 0.02 to 0.15%, Si: at most 0.5%, Mn: 0.5 to 2.5%, and Cu: 0.05 to 1.5% the balance being Fe and impurities;
producing a hollow shell by piercing-rolling the heated round billet;
producing a seamless steel pipe by elongation rolling and sizing the hollow shell;
water cooling the seamless steel pipe at a cooling rate of at least 10° C./sec and stopping water cooling when the temperature of the seamless steel pipe reaches lower than 400° C. to cause bainitic transformation;
heating and soaking the water-cooled seamless steel pipe to cause reverse transformation from a bainite to an austenitic structure;
water cooling the heated and soaked seamless steel pipe; and
tempering the heated, soaked, and water-cooled seamless steel pipe.
2. The method for manufacturing a seamless steel pipe for line pipe according to claim 1 , wherein
the method further comprises a step of heating the produced seamless steel pipe to 900 to 1100° C.; and
in the water cooling step of the heated seamless steel pipe, the heated seamless steel pipe is water cooled.
3. The method for manufacturing a seamless steel pipe for line pipe according to claim 1 , wherein
the chemical composition further comprises one or more types selected from a group of Ni: at most 1.5%, Cr: at most 1.0%, Mo: at most 0.8%, V: at most 0.2%, Nb: at most 0.06%, and Ti: at most 0.05%.
4. The method for manufacturing a seamless steel pipe for line pipe according to claim 2 , wherein
the chemical composition further comprises one or more types selected from a group of Ni: at most 1.5%, Cr: at most 1.0%, Mo: at most 0.8%, V: at most 0.2%, Nb: at most 0.06%, and Ti: at most 0.05%.