High bulk tissue comprising expandable microspheres
View Patent ↗The disclosure relates to high bulk tissue webs containing microspheres. To form the tissue webs, a nonionic polymer dispersion, such as polyvinyl alcohol stabilized vinyl acetate-ethylene copolymer dispersion, is mixed with microspheres and incorporated into tissue webs to increase sheet bulk.
1. An uncreped through-air dried tissue web consisting essentially of cellulosic fibers, a pre-expanded microsphere, a polyvinyl alcohol stabilized vinyl acetate-ethylene copolymer, and a nonionic surfactant, wherein the uncreped through-air dried tissue web has a basis weight from about 20 to about 45 grams per square meter (gsm) and a bulk from about 15 to about 25 cc/g.
2. The tissue web of claim 1 wherein the web comprises less than about 10 percent, by total weight of the web, pre-expanded microspheres.
3. A method of forming an uncreped through air dried high bulk tissue web consisting essentially of the steps:
a. mixing expandable microspheres, a vinyl acetate-ethylene copolymer, polyvinyl alcohol and a surfactant to form a nonionic dispersion polymer;
b. forming a cellulosic fiber slurry;
c. mixing the nonionic dispersion polymer and the cellulosic fiber slurry to form a mixture;
d. disposing the mixture on a forming fabric to form a tissue web; and
e. through-air drying the tissue web, wherein the uncreped through-air dried tissue has a basis weight from about 20 to about 45 gsm and a bulk from about 15 to about 25 cc/g.
4. The method of claim 3 wherein the tissue web comprises less than about 10 percent, by total weight of the web, expandable microspheres.
5. The tissue web of claim 1 wherein the polyvinyl alcohol stabilized vinyl acetate-ethylene copolymer comprises from about 10 to about 35 percent by ethylene and from about 65 to about 90 percent by weight vinyl acetate.
6. The tissue web of claim 1 wherein the web comprises a polyvinyl alcohol having a degree of polymerization from about 200 to about 4,000 and a non-ionic surfactant.
7. The tissue web of claim 1 wherein the web comprises from about 0.5 to about 5 percent, by total weight of the web, pre-expanded microspheres.
8. An uncreped through-air dried tissue web having first, second and third fibrous layer, the second fibrous layer consisting essentially of cellulosic fibers, a pre-expanded microsphere, a polyvinyl alcohol stabilized vinyl acetate-ethylene copolymer, and a nonionic surfactant, and the first and second fibrous layers being substantially free from pre-expanded microspheres, wherein the uncreped through-air dried tissue web has a basis weight from about 20 to about 45 grams per square meter (gsm) and a bulk from about 15 to about 25 cc/g.
9. The tissue web of claim 8 wherein the web comprises from about 0.5 to about 5 percent, by total weight of the web, pre-expanded microspheres.