Method and apparatus for annealing glass plate
View Patent ↗A method and an apparatus for annealing a glass sheet, which can sufficiently reduce I/T formed in the glass sheet, are provided. In the method for annealing a glass sheet G of the present invention, in a state that a heated and bent glass sheet G is placed on a forming mold 16 , first, a region of the glass sheet G to be lifted up is cooled by cooling devices 20, 22 , to make the temperature of the region to be lifted up to be a temperature of at most the strain point. Next, in this state, a lift-up member 36 is operated to lift up the region of the glass sheet G to be lifted up, by rods 38 , to separate the glass sheet G from the forming mold 16.
1. A method for annealing a glass sheet, comprising:
annealing a bent glass sheet that has a high temperature of greater than a strain point and which is supported on a ring-shaped forming mold, while the bent glass sheet is lifted up by a lift-up member and separated from the forming mold; and
lifting up the bent glass sheet with said lift-up member at a region to be lifted which includes a position on the bent glass sheet that contacts with the lift-up member when the lift-up member lifts up the glass sheet, and is a region at least 50 mm inside from an edge of the glass sheet, wherein during said annealing the region to be lifted up is cooled to a temperature below the strain point before the edge of the glass sheet reaches the strain point, and thereafter, the glass sheet is lifted up by the lift-up member.
2. A method for annealing a glass sheet, comprising:
annealing a bent glass sheet that has a high temperature of greater than a strain point and which is supported on a ring-shaped forming mold; and
lifting up the glass sheet by a lift-up member to separate the glass sheet from the forming mold, wherein:
the region to be lifted up by the lift-up member is a region at least 50 mm inside from an edge of the glass sheet, and
during said annealing the region to be lifted up is cooled to a temperature below the strain point before the edge of the glass sheet reaches the strain point, and thereafter, the glass sheet is lifted up by the lift-up member.
3. The method for annealing a glass sheet according to claim 1 , wherein the region to be lifted up is cooled to a temperature below the strain point before the edge of the glass sheet reaches the strain point, and thereafter, the glass sheet is lifted up under the condition that the temperature of a portion 10 mm inside from the edge of the glass sheet is a temperature higher than the strain point −10° C. of the glass sheet.
4. The method for annealing a glass sheet according to claim 2 , wherein the region to be lifted up is cooled to a temperature below the strain point before the edge of the glass sheet reaches the strain point, and thereafter, the glass sheet is lifted up under the condition that the temperature of a portion 10 mm inside from the edge of the glass sheet is a temperature higher than the strain point −10° C. of the glass sheet.
5. The method for annealing a glass sheet according to claim 1 , wherein the region to be lifted up is locally cooled by a radiation cooling device.
6. The method for annealing a glass sheet according to claim 2 , wherein the region to be lifted up is locally cooled by a radiation cooling device.
7. The method for annealing a glass sheet according to claim 5 , wherein the temperature of a surface of the radiation cooling device facing to the glass sheet is controlled to be between 300 and 350° C. to cool the glass sheet.
8. The method for annealing a glass sheet according to claim 6 , wherein the temperature of a surface of the radiation cooling device facing to the glass sheet is controlled to be between 300 and 350° C. to cool the glass sheet.
9. The method for annealing a glass sheet according to claim 1 , wherein two piled up glass sheets are placed on the ring-shaped forming mold.
10. The method for annealing a glass sheet according to claim 2 , wherein two piled up glass sheets are placed on the ring-shaped forming mold.
11. The method according to claim 1 , wherein the glass sheet is annealed in an annealing apparatus disposed in an annealing furnace.
12. The method according to claim 1 wherein the glass sheet is a laminated glass.