Recycling superabsorbent polymer fines
A process is described for recycling superabsorbent polymer fines into a process that includes treating the superabsorbent polymer fines with caustic and a polymerization step for making the superabsorbent polymer gel. The process requires treating the superabsorbent polymer fines with a caustic, followed by mixture with polymerizable monomer solution, and polymerizing the mixture of the superabsorbent polymer fines and monomer to form the aqueous fluid absorbent polymer. In the process, the fines are incorporated into the new polymer gel and become indistinguishable there from. The gel may then be comminuted into a particulate dried and then separated into a portion having a desired minimum particle size in a fines portion having less than the desired size. The particulate may then be coated with a surface crosslinking agent and surface additives and heated for surface conversion.
1. A process for recycling superabsorbent polymer fines in the production of superabsorbent polymer gel, compromising the steps of:
a) dissolving at least one acrylic acid monomer and/or its sodium salt and a cross-linking agent in an aqueous solution to form a monomer solution;
b) polymerizing the mixture obtained in step a) to produce a superabsorbent polymer gel;
c) treating the superabsorbent polymer fines with a caustic solution containing from about 0.1 to about 12% caustic based on the weight of the superabsorbent polymer fines to form caustic treated superabsorbent polymer fines; and
d) mixing the caustic treated superabsorbent polymer fines obtained in step c) with the superabsorbent polymer gel obtained in step b) to provide an aqueous fluid absorbent polymer, wherein the content of the superabsorbent polymer fines relative to the total amount of the superabsorbent polymer gel is from about 0.1 to about 30 wt %.
2. The process of claim 1 further comprising the steps to make a superabsorbent polymer particulate wherein the steps comprise comminuting the aqueous fluid absorbent polymer from said polymerizing and mixing step; drying said comminuted polymer; and separating said dried superabsorbent polymer particulate into a portion having a desired particle size from about 150 μm to about 850 μm as measured by screening through a U.S. standard 20 mesh screen and retained on a U.S. standard 100 mesh screen.
3. The process of claim 2 further comprising the steps to make a superabsorbent polymer composition wherein the steps comprise coating the superabsorbent polymer particulate with a surface crosslinking agent and surface additives; heating said coated polymer; and separating said dried superabsorbent polymer particulate into a portion having a desired particle size from about 150 μm to about 850 μm as measured by screening through a U.S. standard 20 mesh screen and retained on a U.S. standard 100 mesh screen.
4. The process of claim 1 , further comprising the steps of separating the superabsorbent polymer fines having a particle size of less than about 150 μm; treating the superabsorbent polymer fines having a particle size of less than about 150 μm with a caustic solution containing from about 0.1 to about 12% caustic based on the weight of the superabsorbent polymer fines; and recycling said treated superabsorbent polymer fines having a particle size of less than about 150 μm to the polymerizing step b) for forming said superabsorbent polymer gel.
5. The process of claim 3 further comprising the steps of separating the superabsorbent polymer fines having a particle size of less than about 150 μm; treating the superabsorbent polymer fines having a particle size of less than about 150 μm with a caustic solution containing from about 0.1 to about 12% caustic based on the weight of the superabsorbent polymer fines; and recycling said treated superabsorbent polymer fines having a particle size of less than about 150 μm to the polymerizing step b) for forming said superabsorbent polymer gel.
6. The process of claim 1 wherein the caustic is selected from sodium carbonate or sodium bicarbonate.
7. The process of claim 1 wherein said polymer gel is a cross linked polymer of polyacrylic acid, sodium polyacrylate or copolymers thereof.
8. A superabsorbent polymer particulate composition made by the process of claim 3 wherein at least about 40% by weight of the superabsorbent polymer particulate has a particle size from about 300 μm to about 600 μm as measured by screening through a U.S. standard 30 mesh screen and retained on a U.S. standard 50 mesh screen.
9. A superabsorbent polymer particulate composition made by the process of claim 2 having a free swell gel bed permeability of from about 1 to about 70 Darcy.
10. An absorbent composition comprising the superabsorbent polymer particle composition made by the process of claim 3 .
11. A sanitary article comprising the superabsorbent polymer particle composition made by the process of claim 3 .