ANTIREFLECTIVE COATINGS WITH CONTROLLABLE POROSITY AND DURABILITY PROPERTIES USING CONTROLLED EXPOSURE TO ALKALINE VAPOR
In some embodiments, the present invention discloses methods and apparatuses for making coated articles comprising exposing the coated layer to vapor-phase agents to modify its properties, such as the bonding and distribution of the coating mass. The coated layer is a porous solid layer, deposited via methods such as sol-gel, physical or chemical vapor deposition, aerosol deposition, or other methods capable of depositing a porous solid coating, with or without further processing such as curing or heat treatment.
1 . A method of improving an antireflective coating, the method comprising
providing an antireflective coating comprising a porous layer on a transparent substrate;
exposing the porous layer to a vapor environment comprising an alkaline vapor.
2 . A method as in claim 1 wherein the vapor environment further comprises water vapor.
3 . A method as in claim 1 wherein the vapor environment comprises ammonia vapor.
4 . A method as in claim 1 wherein the porous layer is exposed to the vapor environment at room temperature.
5 . A method as in claim 1 further comprising
heat treating the porous layer during the exposure to the vapor environment at a temperature above room temperature.
6 . A method as in claim 1 wherein the porous layer is not subjected to a heat treatment temperature above 300 C before exposing to the vapor environment.
7 . A method as in claim 1 further comprising
removing the substrate from the vapor environment;
heat treating the substrate at a temperature above room temperature.
8 . A method of forming a coated article, the method comprising
providing a transparent substrate;
forming a porous layer on the transparent substrate;
exposing the porous layer to a vapor environment comprising an alkaline vapor.
9 . A method as in claim 8 wherein the vapor environment further comprises water and ammonia vapor.
10 . A method as in claim 8 further comprising
heat treating the porous layer during the exposure to the vapor environment at a temperature above room temperature.
11 . A method as in claim 8 wherein forming a porous layer comprises
coating the substrate with a sol-composition wherein the sol-composition comprises an alkylalkoxysilane-based binder; and
forming a gel on the substrate by drying the sol-formulation.
12 . A method as in claim 8 further comprising
removing the substrate from the vapor environment;
heat treating the substrate at a temperature above room temperature.
13 . A method of forming a coated article, the method comprising
providing a transparent substrate;
coating a layer on the transparent substrate;
curing the coated layer at a first temperature to form a porous layer, wherein the first temperature is above room temperature;
exposing the porous layer to a vapor environment comprising an alkaline vapor.
14 . A method as in claim 13 wherein the vapor environment further comprises water and ammonia vapor.
15 . A method as in claim 13 further comprising
heat treating the porous layer in the vapor environment at a second temperature, wherein the second temperature is above room temperature.
16 . A method as in claim 13 wherein the second temperature is less than or equal to 300 C.
17 . A method as in claim 13 wherein the porous layer is not subjected to a heat treatment temperature above 300 C before exposing the vapor environment.
18 . A method as in claim 13 wherein the layer is coated by a sol-gel process.
19 . A method as in claim 13 wherein coating the layer comprises
coating the substrate with a sol-composition wherein the sol-composition comprises an alkylalkoxysilane-based binder.
20 . A method as in claim 13 further comprising
removing the substrate from the vapor environment;
heat treating the substrate at a third temperature, wherein the third temperature is above room temperature.