Carbon nanofiber, method for production thereof, method for production of carbon fiber composite material using carbon nanofiber, and carbon fiber composite material
View Patent ↗A method of producing a carbon fiber composite material includes a first step and a second step. The first step includes oxidizing first carbon nanofibers produced by a vapor growth method to obtain second carbon nanofibers having an oxidized surface. The second step includes mixing the second carbon nanofibers into an elastomer, and uniformly dispersing the carbon nanofibers in the elastomer by applying a shear force to obtain the carbon fiber composite material. The second carbon nanofibers obtained by the first step have a surface oxygen concentration measured by X-ray photoelectron spectroscopy (XPS) of 2.6 to 4.6 atm %.
1. A carbon fiber composite material produced by providing first carbon nanofibers produced by a vapor growth method;
oxidizing the first carbon nanofibers to obtain second carbon nanofibers having an oxidized surface, the second carbon nanofibers having a surface oxygen concentration measured by X-ray photoelectron spectroscopy (XPS) of 2.6 to 4.6 atm % and a ratio (D/G) of a peak intensity D at around 1300 cm −1 to a peak intensity G at around 1600 cm −1 measured by Raman scattering spectroscopy of 0.12 to 0.22; and mixing
the second carbon nanofibers into an elastomer, and uniformly dispersing the second carbon nanofibers in the elastomer by applying a shear force to obtain a carbon fiber composite material.
2. A carbon fiber composite material comprising an elastomer, and carbon nanofibers having a surface oxygen concentration measured by X-ray photoelectron spectroscopy (XPS) of 2.6 to 4.6 atm % and a ratio (D/G) of a peak intensity D at around 1300 cm −1 to a peak intensity G at around 1600 cm −1 measured by Raman scattering spectroscopy of 0.12 to 0.22.
3. The carbon fiber composite material according to claim 2 , wherein the carbon nanofibers have a specific surface area by nitrogen adsorption of 34 to 58 m 2 /g.
4. The carbon fiber composite material according to claim 1 , wherein the second carbon nanofibers have an average diameter ranging from 60 nm to 150 nm.
5. The carbon fiber composite material according to claim 1 , further comprising obtaining the first carbon nanofibers by pyrolyzing only an organic compound and an organotransition metal compound.
6. The carbon fiber composite material according to claim 5 , wherein the organic compound consists of benzene or toluene and the organotransition metal compound consists of ferrocene or nickelocene.
7. The carbon fiber composite material according to claim 2 , wherein the carbon nanofibers have an average diameter ranging from 60 nm to 150 nm.
8. The carbon fiber composite material according to claim 2 , wherein the carbon nanofibers are obtained by pyrolyzing only an organic compound and an organotransition metal compound.
9. The carbon fiber composite material according to claim 8 , wherein the organic compound consists of benzene or toluene and the organotransition metal compound consists of ferrocene or nickelocene.