Low-carbon steel slab producing method
View Patent ↗A low-carbon steel slab producing method includes: adding Ti to a molten steel decarbonized to have a carbon concentration of 0.05 mass % or less, and subsequently adding at least one of La and Ce to adjust a constitution, and producing a smelted molten steel; and pouring the smelted molten steel into a casting mold via a tundish; wherein at least one of La and Ce in a total amount of 0.2 to 1.2 times an increased amount of oxygen in the smelted molten steel during contained in the tundish is added to the smelted molten steel in the tundish, so as to obtain a steel slab having inclusions which contain oxides of Ti and at least one of La and Ce as chief components, and so as to make a composition of each of the inclusions have a mass ratio of 0.1 to 0.7, in terms of (La 2 O 3 +Ce 2 O 3 )÷TiO n (n=1˜2).
1. A low-carbon steel slab producing method, comprising:
adding Ti without carrying out Al pre-deoxidation to a decarbonized molten steel having a carbon concentration of 0.0013 mass % or less;
subsequently adding at least one of La and Ce to adjust a composition;
producing a smelted molten steel, used for a low-carbon steel slab, containing, by mass %, more than 0% and equal to or less than 0.0013% of carbon, more than 0% and equal to or less than 0.01% of Si, more than 0% and equal to or less than 0.5% Mn, more than 0% and equal to or less than 0.05% P, equal to or more than 0% and equal to or less than 0.02% of S, 0.01% or more and equal to or less than 0.4% of Ti, and in combination, 0.001% or more and 0.01% or less of at least one of La and Ce, and 0.004% or more and 0.02% or less of oxygen, and iron as a base component;
pouring the smelted molten steel into a casting mold via a tundish, wherein
after producing smelted molten steel having inclusions which contain oxides of Ti and at least one of La and Ce as chief components, measuring the oxygen concentration of the molten steel at a downstream of the tundish with an oxygen sensor and determining an increased amount of oxygen in the smelted molten steel picked up during the time the smelted molten steel was contained in the tundish, and continuously adding at least one of La and Ce to the smelted molten steel in the tundish, in wire form, in a total amount of 0.2 to 1.2 times the determined increased amount of oxygen, so as to obtain a steel slab having inclusions which contain oxides of Ti and at least one of La and Ce as chief components with a mass ratio of 0.1 to 0.7, in terms of (La 2 O 3 +Ce 2 O 3 )/TiO n (n=1 to 2).