Porous multi-layer film with improved thermal properties
View Patent ↗Provided is a porous multi-layer film having two or more layers that is used as a separator for battery. In the film, more than 2 layers have different porosities and pore sizes. The film has a thickness of 9 to 50 μm, a machine direction (MD) loop stiffness of 0.008 mg/μm or more, puncture strength of 0.15 N/μm or more, permeability of 1.5×10 −5 Darcy or more, shut-down temperature of 140° C. or less, melt-down temperature of 170° C. or more, a transverse direction (TD) maximum shrinkage of 25% or less in Thermomechanical Analysis (TMA) under a load of 1 mN/(1 μm×6 mm), and melt down temperature of 160° C. or more. Since the porous multi-layer film shows excellent thermal stability at high temperature and electrolyte retaining property due to a dual pore structure, the film shows a superior effect when used as a separator for high-capacity/high-power lithium ion battery.
1. A porous multi-layer film, comprising:
a first layer having a porosity of 30 to 60% and an average pore diameter of 0.01 to 0.1 μm and a second layer adjacent to the first layer, the second layer having a porosity of 50 to 80% and having pores with a pore average plane diameter of 0.1 to 50 μm of 70% or more on the basis of the area of the entire pores of the second layer, wherein the second layer has a thickness of 3 μm or more and occupies 30 to 70% of the entire thickness of the porous multi-layer film, and is prepared to contain a general heat-resistant resin of 50 volume % or more of a resin composition and contain inorganic materials of 30 to 60 wt % together, and the general heat-resistant resin has a melting temperature of 160 to 180° C.; and
the porous multi-layer film has a thickness of 9 to 50 μm, a loop stiffness to the machine direction of 0.008 mg/μm or more, a puncture strength of 0.15 N/μm or more, a permeability of 1.5×10 −5 Darcy or more, a shut-down temperature of 140° C. or less, a melt fracture temperature of 170° C. or more, a maximum shrinkage to a transverse direction (TD) of 25% or less in Thermomechanical Analysis (TMA) under a load of 1 mN/(1 μm×6 mm), and a melt-down temperature (temperature that the length reaches 120%) of 160° C. or more in Thermomechanical Analysis (TMA) under a load of 1 mN/(1 μm×6 mm).
2. The porous multi-layer film of claim 1 , wherein the first layer has a porosity of 40 to 55%, and an average pore diameter of 0.01 to 0.05 μm, and in the second layer, a porosity is 60 to 80% and an area ratio that pores having a pore average plane diameter of 1 to 50 μm occupy in the second layer pore is 70% or more, wherein the entire porous multi-layer film including the first layer and the second layer has a thickness of 12 to 35 μm, and a melt fracture temperature of 180° C. or more.
3. The porous multi-layer film of claim 1 , which is formed of a two-layer porous film having the first layer and the second layer, or a three-layer porous film that the first layers are formed on both surfaces of the second layer, or a three-layer porous film that the second layers are formed on both surfaces of the first layer.
4. The porous multi-layer film of claim 2 , which is formed of a two-layer porous film having the first layer and the second layer, or a three-layer porous film that the first layers are formed on both surfaces of the second layer, or a three-layer porous film that the second layers are formed on both surfaces of the first layer.
5. A porous multi-layer film, comprising:
a first layer having a porosity of 30 to 60% and an average pore diameter of 0.01 to 0.1 μm and a second layer adjacent to the first layer, the second layer having a porosity of 50 to 80% and having pores with a pore average plane diameter of 0.1 to 50 μm of 70% or more on the basis of the area of the entire pores of the second layer,
wherein the second layer has a thickness of 3 μm or more and occupies 30 to 70% of the entire thickness of the porous multi-layer film, and contains a high heat-resistant resin having a melting temperature of 180° C. or more of 50 volume % or more of a resin composition, and other resin of 15 to 50 volume % of the resin composition to be liquid-liquid phase separated from the high heat-resistant resin; and
the porous multi-layer film has a thickness of 9 to 50 μm, a loop stiffness to the machine direction of 0.008 mg/μm or more, a puncture strength of 0.15N/μm or more, a permeability of 1.5×10 −5 Darcy or more, a shut-down temperature of 140° C. or less, a melt fracture temperature of 170° C. or more, a maximum shrinkage to a transverse direction (TD) of 25% or less in Thermomechanical Analysis (TMA) under a load of 1 mN/(1×6 mm), and a melt-down temperature (temperature that the length reaches 120%) of 160° C. or more in Thermomechanical Analysis (TMA) under a load of 1 mN/(1 μm×6 mm).
6. The porous multi-layer film of claim 5 , wherein the first layer has a porosity of 40 to 55%, and an average pore diameter of 0.01 to 0.05 μm, and in the second layer, a porosity is 60 to 80% and an area ratio that pores having a pore average plane diameter of 1 to 50 μm occupy in the second layer pore is 70% or more, wherein the entire porous multi-layer film including the first layer and the second layer has a thickness of 12 to 35 μm, and a melt fracture temperature of 180° C. or more.
7. The porous multi-layer film of claim 5 , which is formed of a two-layer porous film having the first layer and the second layer, or a three-layer porous film that the first layers are formed on both surfaces of the second layer, or a three-layer porous film that the second layers are formed on both surfaces of the first layer.
8. The porous multi-layer film of claim 6 , which is formed of a two-layer porous film having the first layer and the second layer, or a three-layer porous film that the first layers are formed on both surfaces of the second layer, or a three-layer porous film that the second layers are formed on both surfaces of the first layer.