Cationic microfibrillated plant fibre and manufacturing method for same
View Patent ↗The present invention provides a novel cationized microfibrillated plant fiber and a method for manufacturing the same. A cationic microfibrillated plant fiber that is cationically modified with a quaternary-ammonium-group-containing compound, and that has an average diameter of 4 to 200 nm.
1. A method for manufacturing a microfibrillated cellulose fiber cationically modified with a quaternary-ammonium-group-containing compound, the microfibrillated cellulose fiber cationically modified with a quaternary-ammonium-group-containing compound having a degree of substitution of quaternary ammonium groups of not less than 0.03 to less than 0.4 per anhydrous glucose unit and an average diameter of 4 to 200 nm, the method comprising the steps of:
(1) reacting hydroxyl groups in a material containing a cellulose fiber with a quaternary-ammonium-group-containing cationization agent to cationically modify the material containing a cellulose fiber to form a cationically modified cellulose-fiber-containing material, and
(2) defibrating the cationically modified cellulose-fiber-containing material from step (1), in a mixture with water to an extent that a fiber average diameter becomes 4 to 200 nm by using a twin-screw kneader,
wherein the lower limit of the screw circumferential speed of the twin-screw kneader is 45 m/min, and
and wherein the proportion of the cationically modified cellulose-fiber-containing material from step (1) in the mixture subjected to defibration is 10%-70% by weight,
and the method not comprising, between step (1) and step (2), a step of drying the cationically modified cellulose-fiber-containing material.
2. The manufacturing method according to claim 1 , wherein the microfibrillated cellulose fiber cationically modified with a quaternary-ammonium-group-containing compound has a degree of substitution of quaternary ammonium groups of 0.03 to 0.048 per anhydrous glucose unit.
3. The manufacturing method according to claim 1 , wherein the microfibrillated cellulose fiber cationically modified with a quaternary-ammonium-group-containing compound has a degree of Cellulose I crystallinity of 60% or more.
4. The manufacturing method according to claim 1 , wherein the microfibrillated cellulose fiber cationically modified with a quaternary-ammonium-group-containing compound contains lignin in an amount of 0 to 40% by weight.
5. The manufacturing method according to claim 1 , wherein in step (1), the cationically modified cellulose-fiber-containing material and the cationization agent are used in proportions such that the cationization agent is used in an amount of 10 to 1,000 parts by weight per 100 parts by weight of the material containing a cellulose fiber.