Catalyst based on zeolite for producing olefins and for oligomerizing olefins
The invention relates to a novel catalyst based on zeolite, the production of that catalyst, and the use of the catalyst in a method for producing lower olefins from oxygenates and for oligomerizing olefins. The novel catalyst has a SiO 2 /Al 2 O 3 weight ratio of 2 to 9, a BET surface of 250 to 500 m 2 /g, and an Na content under 200 ppm. The catalyst includes a crystalline alumosilicate zeolite and a binder. The catalyst is characterized in that the ratio of the peak heights of its IR absorption bands v=3610 cm −1 ±20 cm −1 /v=3680 cm −1 ±20 cm −1 is greater than 1.8.
1. Catalyst with a SiO 2 /Al 2 O 3 weight ratio from 2 to 9, a BET surface area from 250 to 500 m 2 /g and a Na content of less than 200 ppm, wherein the catalyst comprises a crystalline aluminosilicate zeolite and a binder, characterized in that the ratio of the peak heights of the IR absorption bands v=3610 cm −1 ±20 cm −1 /v=3680 cm −1 ±20 cm −1 of the catalyst is greater than 1.8.
2. Catalyst according to claim 1 , characterized in that the aluminosilicate zeolite has an MFI structure and the binder comprises aluminium oxide.
3. Catalyst according to claim 1 , characterized in that the ratio of the peak heights of the IR absorption bands v=3610 cm −1 ±20 cm −1 /v=3680 cm −1 ±20 cm −1 of the catalyst is 2.0 or greater.
4. The catalyst of claim 3 wherein the ratio of the peak height of the IR bands of the catalyst is between 2.1 and 3.0.
5. Catalyst according to claim 1 , characterized in that the aluminosilicate zeolite is present in an H form.
6. Process for producing the catalyst according to claim 1 , comprising the following steps:
(a) crystallizing an aluminosilicate from an aqueous synthesis suspension, comprising a silicon source, an aluminium source, an alkali source and a template,
(b) separating the aluminosilicate out of the synthesis suspension, followed by a drying step and a calcining step to remove the template from the aluminosilicate;
(c) ion exchanging alkali ions contained in the aluminosilicate in an aqueous medium with a proton-containing substance or a substance that yields protons when heated, wherein the molar ratio of the protons of the proton-containing or proton-yielding substance to aluminium in the aluminosilicate is from 5:1 to 50:1, followed by a drying step;
(d) mixing the ion-exchanged aluminosilicate from stage (c) with a binder to form a product;
(e) shaping the product from stage (d); and
(f) final calcining of the product from stage (e).
7. Process according to claim 6 , wherein in step (c), the obtained ion-exchanged product is separated off, washed with water until the conductivity of the medium is less than 200 μS/cm, and then dried and subjected to an intermediate calcining.
8. Process for producing olefins from oxygenates selected from the group consisting of methanol, dimethyl ether or mixtures thereof, comprising conducting an educt gas over the catalyst of claim 1 .
9. Process for oligomerizing olefins, comprising conducting an educt gas over the catalyst of claim 1 .