Nickel based thermal spray powder and coating, and method for making the same
View Patent ↗Provided in one embodiment includes a multi-fully alloyed powder that provides a wear-resistant and corrosion-resistant coating on a substrate when applied by a thermal spraying process. The coating exhibits desirable hardness, toughness, and bonding characteristics in a highly dense coating that is suitable for a wide range of temperatures. The embodiment provides a method of forming a coating, the method comprising: providing a substrate; and disposing onto the substrate a coating, comprising: a powder-containing composition comprising an alloy, the alloy comprising a solid solution comprising nickel, and a first component comprising at least one transition metal element and at least one nonmetal element.
1. A coating comprising:
an alloy, the alloy comprising a solid solution and a first component, wherein:
the solid solution comprises nickel and chromium,
the first component comprises a binary compound, a ternary compound, or both comprising at least one transition metal element and at least one nonmetal element; and
the alloy is represented by the formula:
(Ni x Cr y ) a (M b N c )
wherein:
M represents the transition metal element in the first component;
N represents the nonmetal element in the first component;
a, b, and c each is greater than 0 and independently represents a weight percentage;
x and y each is greater than 0 and independently represents a weight percentage of the Ni-containing solid solution;
a is from 85 to 95, b is from 0.1 to 10, c is from 5 to 10, a ratio of x to y is between 0.5 to 1.9, and y is 33-35;
wherein the alloy comprises:
48 to 54 wt. % Ni,
33 to 35 wt. % Cr,
3.3 to 3.5 wt. % Si,
4 to 4.5 wt. % B,
about 1 wt. % C,
1-2 wt. % Ti,
and a balance of Fe; and
wherein the coating is substantially amorphous.
2. The coating of claim 1 , wherein the nonmetal element further includes at least one of F, Cl, Br, I, At, O, S, Se, Te, Po, N, P, As, Sb, Bi, Ge, Sn, or Pb.
3. The coating of claim 1 , wherein the transition metal element further includes at least one of Sc, Y, La, Ac, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Tc, Re, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, Au, Zn, Cd, or Hg, or combinations thereof.
4. The coating of claim 1 , wherein the first component comprises at least one of (i) a boride or (ii) a carbide.
5. The coating of claim 1 , further comprising a second component comprising at least one transition metal element and at least one nonmetal element.
6. The coating of claim 1 wherein the coating is fully amorphous.