Activated cathode for hydrogen evolution
View Patent ↗The present invention aims to provide an activated cathode enabling a long-time stable operation with hydrogen overvoltage maintained at a low value, keeping a high remaining rate of the catalyst element after a cease of operation for a short-circuiting and after an electrolysis operation at a high current density, restricting catalyst loss to a little, and having a strong resistance to contamination caused by electrolyte impurity elements. The present invention relates to a cathode for hydrogen evolution with a catalyst layer formed on the cathode substrate, having, at least, three elements comprising platinum, cerium and palladium, as essential element, in a state of metal, metal oxide, or hydroxide, contained, where the mole fraction of respective element being x, y, and z, within a range of 5 mol %≦x≦90 mol %, 5 mol %≦y≦55 mol %, 5 mol %≦z≦65 mol %.
1. A cathode for hydrogen evolution, comprising a catalyst layer formed on a cathode substrate, the catalyst layer comprising platinum, cerium and palladium in a state of metal, metal oxide, or hydroxide, contained within a range of 5 mol %≦x≦90 mol %, 5 mol %≦y≦55 mol %, 5 mol %≦z≦65 mol %, where the mole fractions of platinum, cerium, and palladium respectively are x, y, and z, wherein the catalyst layer comprises a plurality of layers, having an under catalytic coating layer comprising platinum and cerium, and a top catalytic coating layer comprising platinum, cerium and palladium formed on the under catalytic coating layer, with palladium not being present when the under catalytic coating layer is formed, wherein there is more palladium in the top catalytic layer than in the under catalytic layer.
2. The cathode for hydrogen evolution according to claim 1 , wherein lanthanum, in a state of metal, metal oxide, or hydroxide, is present in the catalyst layer.
3. The cathode for hydrogen evolution according to claim 1 , wherein at least one platinum group metal, in a state of metal, metal oxide, or hydroxide, other than platinum and palladium, is present in the catalyst layer.
4. The cathode for hydrogen evolution according to claim 1 , wherein at least one rare earth element other than cerium, in a state of metal, metal oxide, or hydroxide, is present in the catalyst layer.
5. The cathode for hydrogen evolution according to claim 1 , wherein the cerium is present in misch metal.
6. The cathode for hydrogen evolution according to claim 1 , which has a hydrogen overvoltage level below 90 mV at a current density of 5 kA/m 2 .