Rigid biofiber thermoplastic composite and articles made therefrom

1. A compound, comprising:

(1) a coated reinforcing biofiber and

(2) a plastic resin,

wherein the compound, when molded into a plaque has a Flexural Modulus (ASTM D790) of at least 50% more than a compound of uncoated biofiber and the plastic resin, wherein the coated reinforcing biofiber comprises:

(a) biofiber and

(b) plastisol having a Brookfield viscosity (ASTM D1824 25° C., 20 rpm) of about 1200 - 3000 centipoise, and

wherein the coated reinforcing biofiber is present in the compound in a weight percent ranging from about 55% to about 80%.

2. The compound, according to claim 1 , wherein the plastisol, when fused as a resin, has

(1) a Shore D hardness (ASTM D2240-02 after 15 seconds) of more than 60,

(2) a Tensile Strength (ASTM D638) of more than about 48 MPa,

(3) a Percent Elongation (ASTM D638) of less than 10%.

3. The compound of claim 1 , wherein the biofiber comprises plant matter or animal matter.

4. The compound of claim 1 , wherein the biofiber comprises plant matter selected from the group consisting of wood fiber, wood flour, flax, fibrils of grass, fragments of plant shells, fragments of husks, plant pulp, plant hulls, plant seeds, plant fibers, and combinations thereof.

5. The compound of claim 1 , wherein the biofiber comprises animal matter selected from the group consisting of mammalian hair, bone fragments, fragments of animal shells, reptilian hide fragments, and combinations thereof.

6. The compound of claim 1 , wherein the biofiber has an aspect ratio ranging from about 1 to about 100 and a length ranging from about 10 microns to about 6 mm.

7. The compound of any one of claim 3 , wherein the plastisol further comprises heat stabilizers, UV absorbers, fillers, release agents, biocides, pigments, or combinations thereof.

8. The compound of claim 7 , wherein the plastisol, the biofiber, and any optional additives are present in the coated reinforcing biofiber in the following weight percents:

Plastisol

15-50%

Biofiber

50-85%

Optional

0-5%

Additives.

9. The compound of any one of claim 1 , wherein the plastisol is coated on an outer surface of the biofiber but not contacting inner surfaces within the biofiber.

10. The compound of claim 1 , wherein the Flexural Modulus of the compound is at least 3447 MPa.

11. The compound of claim 1 , wherein the Flexural Modulus of the compound exceeds 4826 MPa.

12. The compound of claim 10 , wherein the plastic resin is selected from the group consisting of acrylonitrile-butadiene-styrene (ABS), polyvinyl chloride (PVC), chlorinated polyvinyl chloride (CPVC), polybutylene terephthalate (PBT), polymethyl methacrylate (PMMA), styrene-acrylonitrile (SAN), polyphenylene ether (PPE), polycarbonate (PC), styrene-butadiene-styrene (SBS), acrylic polymers, polyolefins, polymethylmethacrylate (PMMA), polyethylene terephthalate glycol comonomer (PETG), thermoplastic copolyester elastomer (COPE), and combinations thereof.

13. The compound of claim 12 , wherein the plastic resin is in powder form and where the compound is a dry blend of the plastic resin and the coated reinforcing fiber.

14. A shaped article comprising a compound of claim 1 .

15. The shaped article of claim 14 , wherein the compound is extruded or molded into a building material.

16. The shaped article of claim 15 , wherein the building material is a wood plastic composite (WPC) in a shape selected from the group consisting of wall studs, truss supports, beams, windows, doors, fascia, siding, trim, decking, fencing, and ornamental non-load-bearing appurtenances.

17. A building material made of a compound of claim 1 .

18. The compound of claim 2 , wherein the biofiber comprises plant matter or animal matter.

19. The compound of claim 2 , wherein the biofiber comprises plant matter selected from the group consisting of wood fiber, wood flour, flax, fibrils of grass, fragments of plant shells, fragments of husks, plant pulp, plant hulls, plant seeds, plant fibers, and combinations thereof.

20. The compound of claim 2 , wherein the biofiber has an aspect ratio ranging from about 1 to about 100 and a length ranging from about 10 microns to about 6 mm.