Polymer-assisted deposition of films and preparation of carbon nanotube arrays using the films
View Patent ↗Carbon nanotubes were prepared by coating a substrate with a coating solution including a suitable solvent, a soluble polymer, a metal precursor having a first metal selected from iron, nickel, cobalt, and molybdenum, and optionally a second metal selected from aluminum and magnesium, and also a binding agent that forms a complex with the first metal and a complex with the second metal. The coated substrate was exposed to a reducing atmosphere at elevated temperature, and then to a hydrocarbon in the reducing atmosphere. The result was decomposition of the polymer and formation of carbon nanotubes on the substrate. The carbon nanotubes were often in the form of an array on the substrate.
1. A process of preparing an array of carbon nanotubes comprising:
applying a coating solution onto a substrate to form a coated substrate, the coating solution including a soluble metal precursor, a soluble polymer and a suitable solvent, said soluble metal precursor including a first metal selected from iron, nickel, cobalt, and molybdenum, and a second metal selected from aluminum and magnesium, said soluble polymer selected from polyethyleneimine, carboxylated polyethyleneimine, other PEI derivatives, polyacrylic acid, polypyrrolidone, and poly(ethylene-maleic acid); and
heating the coated substrate in a reducing atmosphere including a carbon source gas at temperatures and for time characterized as sufficient to first remove the polymer and after removing the polymer, form an array of carbon nanotubes on the support.
2. The process of claim 1 , wherein the soluble metal precursor further comprises a binding agent selected from ethylenediaminetetraacetic acid and a salt thereof, wherein the soluble metal precursor comprises a complex of the first metal with the binding agent and a complex of the second metal with the binding agent.
3. The process of claim 2 , further comprising forming the coating solution by preparing a first aqueous homogeneous solution by mixing together PEI, a metal salt having a metal selected from Fe, Co, and Ni, a binding agent selected from ethylenediaminetetraacetic acid and a salt thereof, and a suitable solvent to form a solution and then purifying the solution by ultrafiltration to form the first aqueous solution; preparing a second aqueous homogeneous solution by mixing together PEI, a metal salt having a metal selected from Mg and Al, a binding agent selected from ethylenediaminetetraacetic acid and a salt thereof, and a suitable solvent to form a solution and then purifying the solution to ultrafiltration to form a second solution; and
mixing together the first solution and second.
4. The process of claim 2 , wherein said solvent is selected from water, lower alcohols, acetone, tetrahydrofuran, propylene carbonate, acetonitrile, ethylacetate, acetic acid, and mixtures thereof.
5. The process of claim 2 , wherein said solvent is water and is organic-solvent free.
6. The process of claim 2 , wherein said coating solution is applied onto the substrate by spin coating, dipping, spraying, or ink jetting onto the substrate.
7. The process of claim 2 , wherein the substrate comprises silicon.
8. The process of claim 2 , wherein the reducing atmosphere including a carbon containing gas comprises ethylene.
9. A process of preparing an array of carbon nanotubes comprising:
applying a coating solution onto a substrate to form a coated substrate, the coating solution including a soluble metal precursor, a soluble polymer and a suitable solvent, said soluble metal precursor including a first metal selected from iron, nickel, cobalt, and molybdenum, said soluble polymer selected from polyethyleneimine, carboxylated polyethyleneimine, other PEI derivatives, polyacrylic acid, polypyrrolidone, and poly(ethylene-maleic acid); and
heating the coated substrate in a reducing atmosphere including a carbon source gas at temperatures and for time characterized as sufficient to first remove the polymer and after removing the polymer, form an array of carbon nanotubes on the support.
10. The process of claim 9 , wherein the soluble metal precursor further comprises a binding agent selected from ethylenediaminetetraacetic acid and a salt thereof, wherein the soluble metal precursor comprises a complex of the first metal with the binding agent and a complex of the second metal with the binding agent.
11. The process of claim 10 , further comprising forming the coating solution by preparing a first aqueous homogeneous solution by mixing together PEI, a metal salt having a metal selected from Fe, Co, and Ni, a binding agent selected from ethylenediaminetetraacetic acid and a salt thereof, and a suitable solvent to form a solution and then purifying the solution by ultrafiltration to form the first aqueous solution.