High lap shear strength, low back face signature UD composite and the process of making
View Patent ↗Fabrication of ballistic resistant fibrous composites having improved ballistic resistance properties. More particularly, ballistic resistant fibrous composites having high interlaminar lap shear strength between component fiber plies or fiber layers, which correlates to low composite backface signature. The high lap shear strength, low backface signature composites are useful for the production of hard armor articles, including helmet armor.
1. A fibrous composite comprising a plurality of adjoined fiber layers, each fiber layer comprising fibers having surfaces that are at least partially covered with a polymeric material, wherein said fibers are predominantly free of a fiber surface finish; said fibrous composite having an interlaminar lap shear strength between adjoined fiber layers that is greater than the interlaminar lap shear strength between adjoined fiber layers of a comparable fibrous composite having fiber surfaces that are predominantly covered with a fiber surface finish wherein such a fiber surface finish is between the fiber surfaces and the polymeric material.
2. The fibrous composite of claim 1 wherein said composite has an interlaminar lap shear strength between fiber layers of at least about 170 pounds force (lbf) at about room temperature.
3. The fibrous composite of claim 2 wherein said composite comprises polyethylene fibers.
4. The fibrous composite of claim 3 wherein said polymeric material comprises at least one thermoplastic polymer, and wherein said composite comprises fibers having a tenacity of 20 g/denier or more.
5. The fibrous composite of claim 2 wherein said composite comprises a consolidated plurality of cross-plied, non-woven, unidirectional fiber plies, wherein said polymeric material comprises at least one thermoplastic polymeric binder, and wherein each fiber layer of the composite is impregnated with said thermoplastic polymeric binder.
6. The fibrous composite of claim 1 wherein the fiber surfaces are substantially free of a fiber surface finish between the fiber surface and the polymeric material such that said polymeric material is substantially in direct contact with the fiber surfaces, and wherein patches of residual finish are present on the fiber surfaces between the fiber surface and the polymeric material, wherein at least 90% of the fiber surface area is not covered by the residual fiber surface finish.
7. The fibrous composite of claim 1 wherein said polymeric material is physically bonded to the fiber surfaces.
8. The fibrous composite of claim 1 wherein said polymeric material is chemically bonded to the fiber surfaces.
9. The fibrous composite of claim 1 wherein said composite has a composite areal density of from about 3,750 g/m 2 (0.75 psf) to about 12,500 g/m 2 (2.50 psf).
10. The fibrous composite of claim 1 wherein said composite has a backface signature of less than about 8 mm when impacted with a 124-grain, 9 mm FMJ RN projectile fired at a velocity of from about 427 m/s to about 445 m/s (1430 feet/second (fps)±30 fps), wherein the backface signature is measured for a composite having an areal density of 2.0 psf.
11. The fibrous composite of claim 10 wherein said composite has an interlaminar lap shear strength between fiber layers of at least about 170 pounds force (lbf) at about room temperature.
12. The fibrous composite of claim 11 wherein said composite comprises polyethylene fibers.
13. The fibrous composite of claim 12 wherein said polymeric material comprises at least one thermoplastic polymer, and wherein said composite comprises fibers having a tenacity of 20 g/denier or more.
14. The fibrous composite of claim 11 wherein said composite comprises a consolidated plurality of cross-plied, unidirectional fiber plies, wherein said polymeric material comprises at least one thermoplastic polymeric binder, and wherein each fiber layer of the composite is impregnated with said thermoplastic polymeric binder.
15. The fibrous composite of claim 10 wherein the fiber surfaces are substantially free of a fiber surface finish between the fiber surface and the polymeric material such that said polymeric material is substantially in direct contact with the fiber surfaces, and wherein patches of residual finish are present on the fiber surfaces between the fiber surface and the polymeric material, wherein at least 90% of the fiber surface area is not covered by the residual fiber surface finish.
16. The fibrous composite of claim 10 wherein said composite has an interlaminar lap shear strength between fiber layers of at least about 170 pounds force (lbf) at about room temperature and wherein said composite has a backface signature of less than about 8 mm when impacted with a 124-grain, 9 mm FMJ RN projectile fired at a velocity of from about 427 m/s to about 445 m/s (1430 feet/second (fps)±30 fps), wherein backface signature is measured for a composite having an areal density of 2.0 psf.
17. A fibrous composite comprising a plurality of adjoined fiber layers, each fiber layer comprising fibers having surfaces that are at least partially covered with a polymeric material, wherein said fibers are at least partially free of a fiber surface finish such that said polymeric material is at least partially in direct contact with the fiber surfaces; said fibrous composite having an interlaminar lap shear strength between adjoined fiber layers that is greater than the interlaminar lap shear strength between adjoined fiber layers of a comparable fibrous composite comprising a polymeric material which is not at least partially in direct contact with the fiber surfaces.