Injection molding composition and producing method thereof
View Patent ↗An injection molding composition, having a small fluctuation characteristic and a better characteristic, is provided. The above composition is the injection molding composition comprising a ferrite powder which is a collection of ferrite particles, a first binder and a second binder. A weight and a specific surface area of the ferrite powders are represented by Wp and S, and a weight and a density of the first binder and the second binder is represented by Wb 1 , Wb 2 , and Db 1 , Db 2 . A hypothetical thickness Tb 1 of the first binder is 2.0 to 15.0, and a hypothetical thickness Tb 2 of the second binder is 16.5 to 32.0. In the composition, it is preferable that coated ferrite particles coating the outer circumference of the ferrite particles with the first binder and the second binder exist. Tb 1 [nm]=( Wb 1×10 3 )/( Db 1× Wp×S ) formula (1) Tb 2 [nm]=( Wb 2×10 3 )/( Db 2× Wp×S ) formula (2)
1. An injection molding composition comprising:
a soft ferrite powder, which is a collection of ferrite particles;
a first binder; and
a second binder,
wherein:
said first binder is hydrophilic;
said second binder is hydrophobic;
a softening point of said first binder is from 150° C. to 250° C.;
a softening point of said second binder is lower than that of said first binder;
a weight and a specific surface area of said ferrite powders are represented by Wp [g] and S [m 2 /g], a weight and a density of said first binder are represented by Wb 1 [g] and Db 1 [g/cm 3 ], and a weight and a density of said second binder are represented by Wb 2 [g] and Db 2 [g/cm 3 ];
said S is 1.5 to 3.7; and
a hypothetical thickness Tb 1 [nm] of said first binder is calculated by a formula (1) and a hypothetical thickness Tb 2 [nm] of said second binder is calculated by a formula (2), and values obtained therefrom of said Tb 1 is 2.0 to 15.0 and of said Tb 2 is 16.5 to 32.0:
Tb 1=( Wb 1×10 3 )/( Db 1× Wp×S ) formula (1)
Tb 2=( Wb 2×10 3 )/( Db 2× Wp×S ) formula (2).
2. The injection molding composition as set forth in claim 1 , further comprising coated ferrite particles that are coated by said first binder and said second binder.
3. A method of producing an injection molding composition comprising a step of obtaining a mixture by mixing a soft ferrite powder, a first binder and a second binder, wherein:
said first binder is hydrophilic;
said second binder is hydrophobic;
a softening point of said first binder is from 150° C. to 250° C.;
a softening point of said second binder is lower than that of said first binder,
a weight and a specific surface area of said ferrite powders are represented by Wp [g] and S [m 2 /g], a weight and a density of said first binder are represented by Wb 1 [g] and Db 1 [g/cm 3 ], and a weight and a density of said second binder are represented by Wb 2 [g] and Db 2 [g/cm 3 ];
said S is 1.5 to 3.7; and
a hypothetical thickness Tb 1 [nm] of said first binder is calculated by a formula (1) and a hypothetical thickness Tb 2 [nm] of said second binder is calculated by a formula (2), and values obtained therefrom of said Tb 1 is 2.0 to 15.0 and of said Tb 2 is 16.5 to 32.0:
Tb 1=( Wb 1×10 3 )/( Db 1× Wp×S ) formula (1)
Tb 2=( Wb 2×10 3 )/( Db 2× Wp×S ) formula (2).
4. An injection molding composition comprising:
a soft ferrite powder, which is a collection of ferrite particles;
a first binder; and
a second binder,
wherein:
said first binder is a high polymer material selected from the group consisting of polyvinyl acetate, polyvinyl chloride, nylon6, and acryl resin;
said second binder is a high polymer material selected from high density polyethylene, polypropylene, polyacetal, and polystyrene;
a weight and a specific surface area of said ferrite powders are represented by Wp [g] and S [m 2 /g], a weight and a density of said first binder are represented by Wb 1 [g] and Db 1 [g/cm 3 ], and a weight and a density of said second binder are represented by Wb 2 [g] and Db 2 [g/cm 3 ];
said S is 1.5 to 3.7; and
a hypothetical thickness Tb 1 [nm] of said first binder is calculated by a formula (1) and a hypothetical thickness Tb 2 [nm] of said second binder is calculated by a formula (2), and values obtained therefrom of said Tb 1 is 2.0 to 15.0 and of said Tb 2 is 16.5 to 32.0:
Tb 1=( Wb 1×10 3 )/( Db 1× Wp×S ) formula (1)
Tb 2=( Wb 2×10 3 )/( Db 2× Wp×S ) formula (2).
5. A method of producing an injection molding composition comprising a step of obtaining a mixture by mixing a soft ferrite powder, a first binder, and a second binder, wherein:
said first binder is a high polymer material selected from the group consisting of polyvinyl acetate, polyvinyl chloride, nylon6, and acryl resin;
said second binder is a high polymer material selected from high density polyethylene, polypropylene, polyacetal, and polystyrene;
a weight and a specific surface area of said ferrite powders are represented by Wp [g] and S [m 2 /g], a weight and a density of said first binder are represented by Wb 1 [g] and Db 1 [g/cm 3 ], and a weight and a density of said second binder are represented by Wb 2 [g] and Db 2 [g/cm 3 ];
said S is 1.5 to 3.7; and
a hypothetical thickness Tb 1 [nm] of said first binder is calculated by a formula (1) and a hypothetical thickness Tb 2 [nm] of said second binder is calculated by a formula (2), and values obtained therefrom of said Tb 1 is 2.0 to 15.0 and of said Tb 2 is 16.5 to 32.0:
Tb 1=( Wb 1×10 3 )/( Db 1× Wp×S ) formula (1)
Tb 2=( Wb 2×10 3 )/( Db 2× Wp×S ) formula (2).