Coated article with low-E coating having absorbing layers for low film side reflectance and low visible transmission
View Patent ↗Absorbing layers of a low-emissivity (low-E) coating are designed to cause the coating to have a reduced film side reflectance which is advantageous for aesthetic purposes. In certain embodiments, the absorbing layers are metallic or substantially metallic (e.g., NiCr or NiCrN x ) and are positioned in order to reduce or prevent oxidation of the absorbing layers during optional heat treatment (e.g., thermal tempering, heat bending, and/or heat strengthening). Coated articles according to certain example embodiments of this invention may be used in the context of insulating glass (IG) window units, other types of windows, etc.
1. A coated article including a coating supported by a glass substrate, the coating comprising:
first and second infrared (IR) reflecting layers comprising silver, wherein said IR reflecting layers are spaced apart from one another, and wherein the first IR reflecting layer is located closer to the glass substrate than is the second IR reflecting layer;
a first substantially metallic or metallic absorption layer comprising Ni and/or Cr located such that the first absorption layer is located between the first and second IR reflecting layers, wherein the first absorption layer is sandwiched between and contacting first and second dielectric layers comprising silicon nitride;
a second substantially metallic or metallic absorption layer comprising Ni and/or Cr located such that both the first and second IR reflecting layers are located between the glass substrate and the second absorption layer, wherein the second absorption layer is located between and contacting the second IR reflecting layer and a third dielectric layer comprising silicon nitride; and
wherein said first and second substantially metallic or metallic absorption layers each comprise from 0-5% oxygen.
2. The coated article of claim 1 , wherein said first and second absorption layers each comprise NiCr.
3. The coated article of claim 1 , wherein said first and second absorption layers each comprise NiCrN x .
4. The coated article of claim 1 , wherein said first and second absorption layers each comprise from 1-15% nitrogen (atomic %).
5. The coated article of claim 1 , wherein said first and second IR reflecting layers are spaced apart by at least, moving away from the glass substrate: a layer comprising tin oxide, said first layer comprising silicon nitride, said first absorption layer, said second dielectric layer comprising silicon nitride, another layer comprising tin oxide, and a layer comprising zinc oxide.
6. The coated article of claim 1 , wherein no metallic or substantially metallic absorption layer is located between the first IR reflecting layer and the glass substrate.
7. The coated article of claim 1 , wherein only two IR reflecting layers comprising silver are contained in the coating.
8. The coated article of claim 1 , wherein the first absorption layer is from about 35-75 angstroms (Å) thick.
9. The coated article of claim 1 , wherein the second absorption layer is from about 23-48 angstroms (Å) thick.
10. The coated article of claim 1 , wherein the first absorption layer is substantially thicker than the second absorption layer.
11. The coated article of claim 1 , wherein said coated article has a visible transmission of from about 20-43%, measured monolithically.
12. The coated article of claim 1 , wherein said coated article has a visible transmission of from about 24-36%, measured monolithically.
13. The coated article of claim 1 , wherein the coated article is thermally tempered.
14. The coated article of claim 1 , wherein the coated article is not heat treated.
15. The coated article of claim 1 , wherein the coating contains no more than two metallic or substantially metallic absorption layers consisting essentially of NiCr or NiCrN x .
16. The coated article of claim 1 , wherein the third layer comprising silicon nitride is an uppermost layer of the coating.
17. The coated article of claim 1 , wherein said first IR reflecting layer and said first absorption layer are spaced apart by at least, moving away from the glass substrate: a layer comprising an oxide of NiCr, a layer comprising tin oxide, and the first layer comprising silicon nitride.
18. The coated article of claim 1 , wherein the coated article has a visible film side reflectance (RfY), measured monolithically, of less than or equal to 26%.
19. The coated article of claim 1 , wherein the coated article has a visible film side reflectance (RfY), measured monolithically, of less than or equal to 24%.
20. The coated article of claim 1 , wherein a substantially oxided layer comprising an oxide of NiCr is located over and directly contacting the first IR reflecting layer.
21. The coated article of claim 1 , wherein a metallic or substantially metallic layer comprising NiCr and/or NiCrN x is located over and directly contacting the first IR reflecting layer.
22. A coated article including a coating supported by a glass substrate, the coating comprising:
first and second infrared (IR) reflecting layers, wherein said IR reflecting layers are spaced apart from one another, and wherein the first IR reflecting layer is located closer to the glass substrate than is the second IR reflecting layer;
a first substantially metallic or metallic absorption layer located such that the first absorption layer is located between the first and second IR reflecting layers, wherein the first absorption layer is sandwiched between and contacting first and second dielectric layers comprising silicon nitride;
a second substantially metallic or metallic absorption layer located such that both the first and second IR reflecting layers are located between the glass substrate and the second absorption layer, wherein the second absorption layer is located between and contacting the second IR reflecting layer and a third dielectric layer comprising silicon nitride; and
wherein said first and second substantially metallic or metallic absorption layers each comprise from 0-5% oxygen.