Proppant particles formed from slurry droplets and method of use
View Patent ↗Proppant material for hydraulic fracturing is provided. The particles of the proppant are formed by drip casting. A slurry of finely divided ceramic particles is flowed through nozzles and formed into droplets under the influence of vibration. Uniform sized, smooth surface, spherical green particles are formed. The green particles are dried and sintered to form the proppant. The proppant is used in the process of hydraulic fracturing of wells.
1. A method for making proppant particles, comprising:
providing a slurry of bauxite, the slurry containing a reactant comprising a polysaccharide, wherein the slurry has a solids content from about 25 wt % to about 75 wt %;
flowing the slurry through a nozzle in a gas while vibrating the slurry to form droplets;
receiving the droplets in a vessel containing a liquid having an upper surface in direct contact with the gas, the liquid containing a coagulation agent to react with the reactant in the slurry and cause coagulation of the reactant in the droplets;
transferring the droplets from the liquid;
drying the droplets to form green pellets; and
sintering the green pellets in a selected temperature range to form the proppant particles, wherein the proppant particles have an appropriate strength, appropriate strength being defined as a decrease of less than seventy percent of long-term water permeability, as measured in accord with ISO 13503-5 at 250° F., of a pack of test particles, the test particles having the same composition and method of making as the proppant particles, when a stress applied to the pack of test particles increases from 2,000 psi to 14,000 psi and the test particles are in the size range of 20-40 mesh.
2. The method of claim 1 , wherein the proppant particles have a long-term permeability greater than 85 darcies at a stress of 10,000 psi and a temperature of 250° F., as measured in accord with ISO 13503-5.
3. The method of claim 1 , wherein the gas is air.
4. The method of claim 1 , wherein the proppant particles have an average largest pore size of less than about 20 microns.
5. The method of claim 1 , wherein the proppant particles have an average roughness of less than about 2 microns.
6. The method of claim 1 , wherein the proppant particles are formed without the necessity of subjecting the droplets to a sol-gel reaction.
7. The method of claim 1 , wherein the particles are sintered at a temperature in the range from about 1400° C. to about 1650° C.
8. The method of claim 1 , wherein the polysaccharide is an alginate.
9. The method of claim 3 , wherein the slurry further comprises a dispersant and wherein the dispersant is ammonium polyacrylate.
10. The method of claim 1 , wherein the coagulation agent is calcium chloride.
11. The method of claim 1 , wherein the reactant and the coagulation agent react to form a semi-rigid material.
12. The method of claim 1 , wherein the slurry is vibrated as if flows from the nozzle by vibrating the nozzle.
13. The method of claim 1 , wherein the proppant particles are formed without the necessity of subjecting the droplets to a reaction gas free-fall zone.
14. The method of claim 1 , wherein the proppant particles are formed without the necessity of subjecting the droplets to a sol-gel reaction or a reaction gas free-fall zone.