Thick film pastes for fire through applications in solar cells
View Patent ↗Formulations and methods of making solar cell contacts and cells therewith are disclosed. The invention provides a photovoltaic cell comprising a front contact, a back contact, and a rear contact. The back contact comprises, prior to firing, a passivating layer onto which is applied a paste, comprising aluminum, a glass component, wherein the aluminum paste comprises, aluminum, another optional metal, a glass component, and a vehicle. The back contact comprises, prior to firing, a passivating layer onto which is applied an aluminum paste, wherein the aluminum paste comprises aluminum, a glass component, and a vehicle.
1. A method of making a photovoltaic cell comprising:
a. providing a silicon wafer having a first side and a second side,
b. applying a phosphorus source to the first side of the silicon wafer,
c. firing the wafer to form a phosphorus glass layer on the first side of the silicon wafer,
d. removing at least a portion of the phosphorus glass layer from the first side of the silicon wafer,
e. polishing the second side of the silicon wafer,
f. applying a passivating layer to the first and second sides of the wafer,
g. applying to the first side a silver paste comprising, prior to firing,
i. silver,
ii. a glass component, and
iii. a vehicle,
h. applying to the second side an aluminum paste comprising, prior to firing,
i. aluminum,
ii. a glass component, and
iii. a vehicle,
wherein (g) and (h) can be performed in any order, and
i. firing the wafer for a time and temperature sufficient to adhere the silver to the front side and the aluminum to the back side, thereby forming front and back contacts.
2. The method of claim 1 , wherein the aluminum paste further comprises a metal selected from the group consisting of magnesium, nickel, titanium, potassium, vanadium, copper, and combinations thereof.
3. The method of claim 1 , wherein the aluminum paste further comprises a metal selected from the group consisting of palladium, silver, platinum, gold, and combinations thereof.
4. The method of claim 1 , wherein the aluminum paste further comprises a metal selected from the group consisting of boron, gallium, indium, and combinations thereof.
5. The method of claim 1 , wherein the aluminum paste further comprises a metal selected from the group consisting of zinc, tin, indium, antimony and combinations thereof.
6. The method of claim 2 , wherein the aluminum paste comprises about 40 to about 80 wt % aluminum and about 1 to about 50 wt % nickel.
7. The method of claim 2 , wherein the aluminum paste comprises about 40 to about 80 wt % aluminum and about 1 to about 50 wt % magnesium.
8. The method of claim 3 , wherein the aluminum paste comprises about 40 to about 80 wt % aluminum and about 0.1 to about 50 wt % silver.
9. The method of claim 4 , wherein the aluminum paste comprises about 40 to about 80 wt % aluminum and about 0.5 to about 50 wt % boron.