Reduced-VOC and non-VOC blowing agents for making expanded and extruded thermoplastic foams
View Patent ↗A blowing agent blend for making thermoplastic polymer foams includes methyl formate. The blowing agent blend can further comprise at least one co-blowing agent. The co-blowing agent is either a physical co-blowing agent (e.g. an inorganic agent, a hydrocarbon, a halogenated hydrocarbon, a hydrocarbon with polar, functional group(s), water or any combination thereof), or a chemical co-blowing agent, or combinations thereof. The thermoplastic polymer foam can be an alkenyl aromatic polymer foam, e.g. a polystyrene foam. The blowing agent blend includes methyl formate and one or more co-blowing agents. The methyl formate-based blowing agent blends produce dimensionally stable foams that have improved resistance to flame spread. A process for the preparation of such foams is also provided.
1. A thermoplastic polymer foam article prepared by a process comprising:
preparing an expandable polymeric formulation comprising a thermoplastic polymer and a blowing agent blend comprising methyl formate and ethane, the blowing agent blend comprising about 70 to about 87 weight percent of methyl formate; and
expanding the formulation to form a substantially closed-cell, dimensionally stable foam article.
2. The thermoplastic polymer foam article of claim 1 , wherein the thermoplastic polymer foam article is a sheet.
3. The thermoplastic polymer foam article of claim 2 , wherein the sheet is thermoformable.
4. The thermoplastic polymer foam article of claim 1 , wherein the blowing agent blend comprises about 13 to about 30 weight percent of ethane.
5. The thermoplastic polymer foam article of claim 1 , wherein the thermoplastic polymer is an alkenyl aromatic polymer.
6. The thermoplastic polymer foam article of claim 1 , wherein the thermoplastic polymer is an amorphous polymer selected from the group consisting of polystyrene, polycarbonate, poly(methyl methacrylate), poly(phenylene oxide), and mixtures thereof.
7. The thermoplastic polymer foam article of claim 1 , wherein the thermoplastic polymer foam article has a substantially uniform density.
8. The thermoplastic polymer foam article of claim 1 , wherein the thermoplastic polymer foam article has a density of about 1 lb/ft 3 to about 15 lb/ft 3 .
9. A process for producing a thermoplastic polymer foam article comprising:
preparing an expandable polymeric formulation comprising a thermoplastic polymer and a blowing agent blend comprising methyl formate and ethane, the blowing agent blend comprising about 70 to about 87 weight percent of methyl formate; and
expanding the formulation to form a substantially closed-cell, dimensionally stable foam article.
10. The process of claim 9 , wherein preparing the expandable polymeric formulation comprises:
melting the thermoplastic polymer; and
dissolving an effective amount of the blowing agent blend in the thermoplastic polymer to define the formulation.
11. The process of claim 9 , wherein the thermoplastic polymer foam article is a sheet.
12. The process of claim 11 , wherein the sheet is thermoformable.
13. The process of claim 9 , wherein the blowing agent blend comprises about 13 to about 30 weight percent of ethane.
14. The process of claim 9 , wherein the thermoplastic polymer is an alkenyl aromatic polymer.
15. The process of claim 9 , wherein the thermoplastic polymer is an amorphous polymer selected from the group consisting of polystyrene, polycarbonate, poly(methyl methacrylate), poly(phenylene oxide), and mixtures thereof.
16. The process of claim 9 , wherein the thermoplastic polymer foam article has a substantially uniform density.
17. The process of claim 9 , wherein the thermoplastic polymer foam article has a density of about 1 lb/ft 3 to about 15 lb/ft 3 .