Dispersions of silicon nanoparticles
View Patent ↗Inorganic particle/polymer composites are described that involve chemical bonding between the elements of the composite. In some embodiments, the composite composition includes a polymer having side groups chemically bonded to inorganic particles. Furthermore, the composite composition can include chemically bonded inorganic particles and ordered copolymers. Various electrical, optical and electro-optical devices can be formed from the composites.
1. A dispersion comprising a liquid and from about 0.075 weight percent to about 30 weight percent silicon nanoparticles having an average primary particle diameter from about 5 nm to about 100 nm.
2. The dispersion of claim 1 wherein at least about 95 percent of the silicon particles have a size that is greater than about 40 percent of the average primary particle size and that is less than about 160 percent of the average primary particle size.
3. The dispersion of claim 1 wherein the silicon nanoparticles have an average primary particle size from about 2 nm to about 50 nm.
4. The dispersion of claim 1 wherein the dispersion is stable.
5. The dispersion of claim 1 wherein the dispersion further comprises a polymer.
6. The dispersion of claim 5 wherein the polymer is selected from the group consisting of polyamides, polyimides, polycarbonates, polyurethanes, polyacrylonitrile, polyacrylic acid, polyacrylates, polyacrylamides, polyvinyl alcohol, polyvinyl chloride, heterocyclic polymers, polyesters, and modified polyolefins.
7. The dispersion of claim 6 wherein the polymer comprises polysilane or polysiloxane.
8. The dispersion of claim 1 wherein the silicon nanoparticles comprise crystalline silicon nanoparticles.
9. A dispersion comprising an alcohol and from about 0.1 weight percent to about 30 weight percent silicon nanoparticles having an average primary particle diameter of about 2 nm to about 100 nm, wherein the dispersion is stable; and
wherein at least about 95 percent of the silicon particles have a size that is greater than about 40 percent of the average primary particle size and that is less than about 160 percent of the average primary particle size.
10. The dispersion of claim 9 wherein the silicon nanoparticles have an average secondary particle size of less than about 500 nm.
11. The dispersion of claim 9 wherein the silicon nanoparticles have an average primary particle size from about 2 nm to about 50 mn.
12. The dispersion of claim 9 further comprising a polymer.
13. The dispersion of claim 9 further comprising a polysilane or a polysiloxane.
14. A dispersion comprising a liquid, silicon nanoparticles having an average primary particle diameter of about 2 nm to about 100 mn and a polysiloxane, wherein at least about 95 percent of the silicon particles have a size that is greater than about 40 percent of the average primary particle size and that is less than about 160 percent of the average primary particle size.
15. The dispersion of claim 14 wherein the polysiloxane comprises polydimethylsiloxane.
16. The dispersion of claim 14 wherein the silicon nanoparticles have an average primary particle diameter from about 2 nm to about 50 nm and wherein the dispersion has from about 0.075 weight percent to about 30 weight percent silicon nanoparticles.
17. The dispersion of claim 14 wherein the liquid comprises an alcohol.