Orthodontic adhesives
View Patent ↗An orthodontic adhesive includes a curable resin monomer component; a quaternary curing initiator system; and filler. Another orthodontic adhesive having a W/C ratio (working time to curing time ratio) of at least 10, 12, 14 or 20, includes a curable resin monomer component; a curing initiator system; and filler. The adhesives are suitable as light-curing and may include a colorant. Suitable colorants include reversible, thermochromic dyes. The adhesive may also include a resin toughening component.
1. A method of bonding an orthodontic appliance to a tooth surface, comprising:
etching the tooth surface;
applying a bonding sealant to the tooth surface;
applying a single component light-curable orthodontic adhesive to a surface of the orthodontic appliance;
positioning the orthodontic appliance on the tooth surface such that the adhesive is located between the appliance and the bonding sealant; and
light curing the orthodontic adhesive, wherein the adhesive comprises:
a curable resin monomer component;
a quaternary curing initiator system comprising:
camphorquinone and bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide,
octyldimethylaminobenzoate, and
1,1′-azobis(cyanocyclohexane); and
filler.
2. The method of claim 1 , wherein the orthodontic adhesive further comprises a colorant.
3. The method of claim 2 , wherein said colorant includes at least one reversible dye.
4. The method of claim 3 , wherein said reversible dye is thermochromatic.
5. The method of claim 4 , wherein said reversible, thermochromatic dye has a readily visible, non-tooth colored color below its clearing temperature and is generally tooth colored at body temperature.
6. The method of claim 1 , wherein the orthodontic adhesive further comprises a resin toughening component.
7. The method of claim 6 , wherein said resin toughening component is a methacrylated urethane resin.
8. The method of claim 6 , wherein said resin toughening component is an acrylic terminated polyurethane.
9. The method of claim 1 , wherein said curable resin monomer component includes at least two of the following: bisphenol A diglycidyl ether dimethacrylate, ethoxylated bisphenol A dimethacrylate, ethoxylated trimethylopropane triacrylate, pyromellitic glycol dimethacrylate, triethylene glycol dimethacrylate, glycidyl methacrylate, and glycerol dimethacrylate.
10. The method of claim 1 , wherein the single component light-curable orthodontic adhesive will not harden to a crusty consistency for about 70 seconds to about 100 seconds when exposed to a halogen operatory exam lamp positioned at a distance providing 10,000 ±50 lux output for an approximately 2 mm×2 mm×20 mm extruded sample of the adhesive on a white background; and wherein the single component light-curable orthodontic adhesive is capable of exhibiting a shear bond strength, when applied to an etched and sealed bovine tooth, of greater than 7 MPa within 60 seconds after light curing for a duration of 2 seconds to 5 seconds, as measured using a halogen curing light having an 850 mW/cm 2 output in the 400-505 nm range to irradiate the adhesive applied to an etched and sealed bovine tooth.
11. The method of claim 1 , wherein the single component light-curable orthodontic adhesive has a working time (W) to curing time (C) ratio (W/C) of at least 10 to 30,
wherein said working time is expressed as a multiple of a five second intervals that is visually determined as a point at which an approximately 2 mm×2 mm extruded sample of the single component light-curable orthodontic adhesive sufficiently hardens to a crusty consistency and undergoes a brittle fracture when cut in approximately 2 mm sections under a halogen operatory exam light positioned to provide 10,000 ±50 lux at the extruded sample on a white background, and
wherein said curing time is a duration of exposing the single component light-curable orthodontic adhesive to a curing light that is necessary to effect a shear bond strength greater than 7 MPa within 60 seconds after the single component light-curable orthodontic adhesive is applied to an etched and sealed bovine tooth.
12. The method of claim 11 , wherein the curing light is a halogen curing light having an 850 mW/cm 2 output in the 400-505 nm range.
13. The method of claim 1 , wherein etching the tooth surface comprises contacting the tooth surface with 37% phosphoric acid.
14. The method of claim 1 , wherein the quaternary curing initiator system comprises:
0.04 wt % to 0.05 wt % camphorquinone,
0.5 wt % to 0.6 wt % bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide,
0.06 wt % to 0.07 wt % octyldimethylaminobenzoate, and
0.2 wt % 1,1′-azobis(cyanocyclohexane), wherein wt % is based on the entire weight of the single component light-curable orthodontic adhesive.