METAL MICROPARTICLES AND METHOD FOR PRODUCING THE SAME, METAL PASTE CONTAINING THE METAL MICROPARTICLES, AND METAL COAT MADE OF THE METAL PASTE
To provide metal microparticles, with less content of alkali metal, halogen, sulfur, and phosphorus as impurities, wherein surfaces thereof are coated with a protective agent, and the protective agent is selected from at least one type of an amine compound and a calboxylic acid compound, and a total content of the alkali metal, halogen, sulfur, and phosphorus contained in the metal microparticles is less than 0.1 mass % relative to a mass of the metal microparticles.
1 . Metal microparticles with surfaces coated with a protective agent, wherein the protective agent is selected from at least one type of an amine compound and a carboxylic acid compound, and a total content of alkali metal, halogen, sulfur, and phosphorus contained in the metal microparticles is less than 0.1 mass % relative to a mass of the metal microparticles.
2 . The metal microparticles according to claim 1 , wherein the protective agent is composed of an amine compound and a calboxylic acid compound.
3 . The metal microparticles according to claim 1 , wherein the amine compound is an aliphatic amine compound represented by a general formula NH 2 R 1 , NHR 1 R 2 , or NR 1 R 2 R 3 , in which R 1 , R 2 , and R 3 indicate carbon numbers 2 to 16.
4 . The metal microparticles according to claim 1 , wherein the metal microparticles are composed of at least one type of gold, silver, copper, platinum, or palladium.
5 . A metal paste containing the metal microparticles of claim 1 and a solvent composition.
6 . The metal paste according to claim 5 , wherein the solvent composition is selected from one type of water, alcohols, aldehydes, ethers, esters, amines, monosaccharide, straight-chain hydrocarbon, fatty acids, and aromatics, or a combination of them.
7 . A metal coat, which is formed by sintering the metal paste of claim 5 .
8 . A method for producing metal microparticles, comprising the steps of:
reducing and precipitating a metal nucleus from a metal compound dispersed in a solid state, in a liquid phase containing a reducing agent and a protective agent, and agglutinating the metal nucleus, and coating the metal nucleus with the protective agent, and generating metal microparticles; and
removing alkali metal, halogen, sulfur, and phosphorus, being impurities contained in the metal microparticles;
wherein at least one type of an amine compound and a calboxylic acid compound not containing the impurities is used in the generating step, as the reducing agent and the protective agent, and
a mixed solvent of water and an organic solvent is used in the purifying step,
so that a total content of the impurities is less than 0.1 mass % relative to a mass of the metal microparticles.
9 . The method for producing metal microparticles according to claim 8 , wherein the amine compound and the calboxylic acid compound not containing the impurities are used in the generating step, as the protective agent.
10 . The method for producing metal microparticles according to claim 8 , wherein the metal compound is a metal oxide.