Process for obtaining precipitated calcium carbonate
The present invention provides a process for preparing a precipitated calcium carbonate product. The process comprises the steps of preparing an aqueous suspension of precipitated calcium carbonate seeds by carbonating a suspension of Ca(OH) 2 in the presence of 0.005 to 0.030 moles of Sr, in the form of Sr(OH) 2 , based upon moles of Ca(OH) 2 prior to or during carbonation; forming an aqueous suspension of a precipitated calcium carbonate product by carbonating a slurry of Ca(OH) 2 in the presence of 0.5 to 5% by dry weight of the precipitated calcium carbonate seeds, wherein the precipitated calcium carbonate seeds have a D50 that is less than the D50 of the precipitated calcium carbonate product and the precipitated calcium carbonate seeds have an aragonitic polymorph content greater than or equal to the precipitated calcium carbonate product.
1. A process for preparing a precipitated calcium carbonate product comprising the steps of:
(a) preparing an aqueous suspension of precipitated calcium carbonate seeds by carbonating a suspension of Ca(OH) 2 in the presence of 0.005 to 0.030 moles of Sr, in the form of Sr(OH) 2 , per mole of Ca(OH) 2 ; and
(b) forming an aqueous suspension of a precipitated calcium carbonate product by carbonating a slurry of Ca(OH) 2 in the presence of 0.5 to 5% by dry weight of the precipitated calcium carbonate seeds based on the dry weight of Ca(OH) 2 ,
wherein the precipitated calcium carbonate seeds have a D50 that is less than the D50 of the precipitated calcium carbonate product and the precipitated calcium carbonate seeds have an aragonitic polymorph content greater than or equal to the precipitated calcium carbonate product.
2. The process of claim 1 , wherein the suspension of Ca(OH) 2 in step (a) is carbonated in the presence of 0.01 to 0.02 moles of Sr per mole of Ca(OH) 2 .
3. The process of claim 1 , wherein the Sr(OH) 2 in step (a) is formed in situ by the addition of a SrO—comprising mineral.
4. The process of claim 3 , wherein the SrO—comprising mineral is obtained by calcinating a SrCO 3 —comprising mineral.
5. The process of claim 1 , further comprising the step of performing one or more of dewatering, dispersion, or grinding, of the precipitated calcium carbonate seeds prepared in step (a) to obtain an aqueous suspension of precipitated calcium carbonate seeds having a D50 of less than or equal to 0.1 to 0.3 μm and a BET SSA of 10 to 30 m 2 /g.
6. The process of claim 1 , wherein the aqueous solution of precipitated calcium carbonate seeds formed in step (a) has an aragonitic polymorph content of greater than 85% by dry weight.
7. The process of claim 1 , wherein the aqueous solution of precipitated calcium carbonate seeds formed in step (a) has an aragonitic polymorph content of greater than 90% by dry weight.
8. The process of claim 1 , wherein the aqueous solution of precipitated calcium carbonate seeds formed in step (a) has an aragonitic polymorph content of greater than 95% by dry weight.
9. The process of claim 1 , wherein the precipitated calcium carbonate seeds are added to the slurry of Ca(OH) 2 in step (b) prior to carbonation.
10. The process of claim 1 , further comprising the step of performing one or more of dewatering, dispersion, or grinding, of the precipitated calcium carbonate product obtained in step (b) to obtain a precipitated calcium carbonate product having a D50 of between 0.35 and 0.4 microns and a BET SSA of between 8 and 20 m 2 /g.
11. The process of claim 1 , wherein the precipitated calcium carbonate product obtained in step (b) has a total strontium quantity of 0.2 to 15 mol/dry metric ton.
12. The process of claim 1 , wherein the precipitated calcium carbonate product obtained in step (b) has a total strontium quantity of 1 to 5 mol/dry metric ton.
13. The process of claim 1 , wherein the precipitated calcium carbonate product obtained in step (b) contains an aragonitic polymorph content of greater than 60% by dry weight.
14. The process of claim 1 , wherein the precipitated calcium carbonate product obtained in step (b) contains an aragonite polymorph content of greater than 70% by dry weight.