STEEL SHEET FOR CONTAINER AND METHOD OF MANUFACTURING THE SAME
The present invention provides a steel sheet for a container including: a plated layer containing an adhesion amount of 300 to 1000 mg/m 2 of nickel, provided on at least one surface of a steel sheet as metal Ni; and a chemical conversion treatment film formed on the steel sheet by performing immersion or a cathodic electrolytic treatment with a solution containing Zr ions, F ions, and phosphate ions, wherein a metal Zr adhesion amount of the chemical conversion treatment film is 1.0 to 50 mg/m 2 , an amount of 0.5 to 25 mg/m 2 of a phosphate compound is contained in terms of P amount, and an F-atom number density measured by XPS analysis of a plane of 2 nm and a plane of 4 nm in a depth direction obtained by a sputtering treatment is equal to or less than 2 at %.
1 . A steel sheet for a container comprising:
a plated layer containing an adhesion amount of 300 to 1000 mg/m 2 of a nickel, provided on at least one surface of a steel sheet as a metal Ni; and
a chemical conversion treatment film formed on the steel sheet by performing an immersion or a cathodic electrolytic treatment with a solution containing Zr ions, F ions, and phosphate ions,
wherein a metal Zr adhesion amount of the chemical conversion treatment film is 1.0 to 50 mg/m 2 ,
an amount of 0.5 to 25 mg/m 2 of a phosphate compound is contained in terms of P amount, and
an F-atom number density measured by XPS analysis of a plane of 2 nm and a plane of 4 nm in a depth direction obtained by a sputtering treatment is equal to or less than 2 at %.
2 . The steel sheet for a container according to claim 1 ,
wherein the plated layer contains an adhesion amount of 100 to 15000 mg/m 2 of tin as metal Sn.
3 . A method of manufacturing the steel sheet for a container according to claim 1 , the method comprising:
forming the chemical conversion treatment film on the steel sheet by performing an immersion or a cathodic electrolytic treatment with the solution, and thereafter performing a washing treatment with a warm water at 40° C. or higher for 0.5 or more seconds.
4 . A method of manufacturing the steel sheet for a container according to claim 1 , the method comprising:
performing washing with a water at a temperature of equal to or higher than 20° C. and equal to or less than 60° C. for 0.1 or more seconds, and thereafter performing a washing treatment with a warm water at 40° C. or higher for 0.5 or more seconds.
5 . A method of manufacturing the steel sheet for a container according to claim 2 , the method comprising:
forming the chemical conversion treatment film on the steel sheet by performing an immersion or a cathodic electrolytic treatment with the solution, and thereafter performing a washing treatment with a warm water at 40° C. or higher for 0.5 or more seconds.
6 . A method of manufacturing the steel sheet for a container according to claim 2 , the method comprising:
performing washing with a water at a temperature of equal to or higher than 20° C. and equal to or less than 60° C. for 0.1 or more seconds, and thereafter performing a washing treatment with a warm water at 40° C. or higher for 0.5 or more seconds.