Steel sheet for container excellent in corrosion resistance
View Patent ↗According to the present invention, a steel sheet for a container excellent in corrosion resistance, adhesion, and weldability is provided, which includes a steel sheet; a Ni plating layer which is formed on a surface of the steel sheet in an amount of plating deposition containing a Ni amount of 0.3 to 3 g/m 2 and contains Co in the range of 0.1 to 100 ppm; and a chromate coating layer which is formed on a surface of the Ni plating layer in an amount of coating deposition containing a converted Cr amount of 1 to 40 mg/m 2 .
1. A steel sheet for a container excellent in corrosion resistance, adhesion, and weldability, the steel sheet comprising:
a steel sheet;
a Ni plating layer of which surface is formed directly on a surface of the steel sheet, consisting of 0.3 to 3 g/m 2 of Ni, 0.1 to 100 ppm by mass of Co with respect to the Ni plating layer, and inevitable impurities; and
a chromate coating layer which is formed directly on a surface of the Ni plating layer, containing a converted metallic Cr amount of 1 to 40 mg/m 2 .
2. The steel sheet for the container according to claim 1 , wherein the Ni plating layer contains 0.35 to 2.8 g/m 2 of Ni.
3. The steel sheet for the container according to claim 1 or 2 , wherein the Ni plating layer contains 0.3 to 92 ppm by mass of Co.
4. The steel sheet for the container according to claim 1 or 2 , wherein the chromate coating layer contains a converted metallic Cr amount of 1.2 to 38 mg/m 2 .
5. A steel sheet for a container excellent in corrosion resistance, adhesion, and weldability, the steel sheet comprising:
a steel sheet;
a Ni plating layer of which surface is formed directly on a surface of the steel sheet, consisting of 0.3 to 3 g/m 2 of Ni, 0.1 to 100 ppm by mass of Co with respect to the Ni plating layer, and inevitable impurities; and
a Zr-containing coating layer which is formed directly on a surface of the Ni plating layer, containing a converted metallic Zr amount of 1 to 40 mg/m 2 .
6. The steel sheet for the container according to claim 5 , wherein the Ni plating layer contains 0.42 to 2.4 g/m 2 of Ni.
7. The steel sheet for the container according to claim 5 or 6 , wherein the Ni plating layer contains 0.1 to 89 ppm by mass of Co.
8. The steel sheet for the container according to claim 5 or 6 , wherein the Zr-containing coating layer contains a converted metallic Zr amount of 1 to 37 mg/m 2 .