Apparatus for producing metal oxide nanofibers and method for producing metal oxide nanofibers
View Patent ↗An apparatus for producing metal oxide nanofibers includes a jetting unit, a mixing unit, a heating unit, and a cooling unit. The jetting unit jets particles made of a metal. The mixing unit prepares a mixture by mixing the metal particles and a gas containing an oxidizing component that includes oxygen in molecules of the component. The heating unit heats the mixture to raise the temperature of the mixture up to a temperature at which the metal evaporates. The cooling unit cools the product thus-produced in the heating unit.
1. A method for producing metal oxide nanofibers, the method comprising steps of:
jetting particles made of a first metal;
preparing a mixture by mixing the particles and a gas containing an oxidizing component including oxygen in a molecule of the oxidizing component;
heating the mixture to raise a temperature of the mixture up to a temperature at which the first metal evaporates and is suboxidized, the first metal is suboxidized to form a suboxide of the first metal; and
cooling the suboxide formed by the heating so as to form metal oxide nanofibers,
wherein in cooling the suboxide formed by the heating, the suboxide is cooled and further oxidized into oxide in the gas containing the oxidizing component, and thereby forming the metal oxide nanofibers, and the first metal is one of Si, Ti, and Al.
2. The method for producing metal oxide nanofibers according to claim 1 , wherein the particles made of the first metal are jetted in a state of the mixture.
3. The method for producing metal oxide nanofibers according to claim 1 , wherein, when the mixture is prepared, the jetted particles and the gas are mixed.
4. The method for producing metal oxide nanofibers according to claim 1 , wherein preparing the mixture and heating the mixture are carried out by heating the jetted particles in an atmosphere of the gas.
5. The method for producing metal oxide nanofibers according to claim 1 , wherein the cooled product is received by an object for the nanofibers to adhere to a surface of the object.
6. The method for producing metal oxide nanofibers according to claim 1 , wherein the cooled product is received by a reservoir for the nanofibers to be stored in the reservoir.
7. The method for producing metal oxide nanofibers according to claim 1 , wherein, when the particles are heated, the particles are in contact only with the gas.
8. The method for producing metal oxide nanofibers according to claim 1 , wherein, when the particles of the first metal are jetted, the particles of the first metal and particles of a second metal having a higher boiling point than that of the first metal are mixed and jetted.
9. The method for producing metal oxide nanofibers according to claim 1 , wherein, the gas, the particles of the first metal, and particles of a second metal having a higher boiling point than that of the first metal are mixed, when the gas and the particles of the first metal are mixed together for preparing the mixture.
10. The method for producing metal oxide nanofibers according to claim 1 , wherein the first metal is Si.
11. A method for producing silicon dioxide nanofibers, the method comprising steps of:
jetting metallic silicon particles;
preparing a mixture by mixing the metallic silicon particles and a gas containing an oxidizing component including oxygen in a molecule of the oxidizing component;
heating the mixture to raise a temperature of the mixture up to a temperature at which the metallic silicon particles evaporate and are suboxidized to form a silicon suboxide; and
cooling the silicon suboxide and further oxidizing the silicon suboxide in the gas containing the oxidizing component, and thereby forming the silicon dioxide nanofibers.