Thermally expandable microcapsule
The present invention provides a thermally expandable microcapsule that maintains a high expansion ratio and hardly bursts and shrinks even at a high temperature, a foamable thermoplastic resin masterbatch and a foam molded product that are produced using the thermally expandable microcapsule, and a method for producing the thermally expandable microcapsule. The thermally expandable microcapsule comprises a volatile expansion agent included in a shell as a core agent and the shell formed of a polymer, the shell containing a thermosetting resin and a polymer obtainable by polymerization of a monomer composition containing a nitrile-type monomer and a monomer having a carboxyl group, and the thermosetting resin having no radical-polymerizable double bond and at least two functional groups reactive with a carboxyl group per molecule.
1. A thermally expandable microcapsule comprising a volatile expansion agent included in a shell as a core agent and the shell formed of a polymer, wherein
the shell contains a thermosetting resin and a polymer obtained by polymerization of a monomer composition containing a nitrile-type monomer and a monomer having a carboxyl group,
the thermosetting resin has no radical-polymerizable double bond and at least two functional groups reactive with a carboxyl group per molecule,
an amount of the thermosetting resin is 0.01 to 30% by weight relative to entire polymers constituting the shell,
an amount of the monomer having a carboxyl group is 1 to 50 parts by weight relative to 100 parts by weight of the monomer composition, and
the thermosetting resin has a gel fraction of less than 5% at T1.0 and a gel fraction of not less than 5% at T1.5, wherein T1.0 indicates a temperature when the core agent shows a vapor pressure of 1.0 MPa and T1.5 indicates a temperature when the core agent shows a vapor pressure of 1.5 MPa.
2. The thermally expandable microcapsule according to claim 1 ,
wherein the functional groups reactive with a carboxyl group are epoxy groups.
3. A foamable thermoplastic resin masterbatch,
which comprises the thermally expandable microcapsule according to claim 1 , and a thermoplastic resin.
4. A foam molded product,
which is produced with the thermally expandable microcapsule according to claim 1 .
5. A method for producing the thermally expandable microcapsule according to claim 1 ,
which comprises the steps of:
preparing an aqueous dispersion medium;
dispersing in the aqueous dispersion medium an oily mixture containing a monomer composition containing a nitrile-type monomer and a monomer having a carboxyl group, a thermosetting resin having no radically polymerizable double bond and at least two functional groups reactive with a carboxyl group per molecule, and a volatile expansion agent; and
polymerizing the monomer composition,
wherein the thermosetting resin has a gel fraction of less than 5% at T1.0 and a gel fraction of not less than 5% at T1.5, wherein T1.0 indicates a temperature when the core agent shows a vapor pressure of 1.0 MPa and T1.5 indicates a temperature when the core agent shows a vapor pressure of 1.5 MPa.
6. A foam molded product,
which is produced with the foamable thermoplastic resin masterbatch according to claim 3 .